Nitrogen-Enriched Porous Polyacrylonitrile-Based Carbon Fibers for CO2 Capture
文献类型：期刊论文
| 作者 | Li, De-Hong; Zhang, Yong-Gang; Li, Li; Wang, Xue-Fei; Zhong, Jun-Jun; Qian, Xin; Song, Shu-Lin |
| 刊名 | INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH
 |
| 出版日期 | 2018 |
| 卷号 | 57期号:34页码:11608-11616 |
| 关键词 | Activated Carbon Dioxide Capture Combining Ammoxidation Surface-chemistry Koh Activation Pan Fiber Pore-size Adsorption Nanofibers Polyvinylpyrrolidone |
| 英文摘要 | Utilizing porous polyacrylonitrile (PAN) fibers as the precursors, porous carbon fibers were obtained by cross-linking of precursor fibers with hydrazine hydrate and subsequent heat treatment. A nitrogen content of more than 14 wt % was achieved in the carbon fibers. The porous carbon fiber that was prepared at low concentration of hydrazine hydrate (5 wt %) showed an optimal BET surface area of 277.4 m(2)/g with micro-/meso-/macropores. The CO2 adsorbed amount of this porous carbon fiber was 101 mg/g at 25 degrees C under atmospheric pressure, which was 2.1 times that of the fiber without cross-linking with hydrazine hydrate. In the simulated flue gas environment (10% CO2/90% N-2), the adsorption capacity of the above-mentioned porous fiber was 32 mg/g at 25 degrees C, which was 1.4 times that of the fiber without cross-linking. These CO2 adsorption results demonstrated that the nitrogen functionalities and porous structure of the porous carbon fiber played an equivalent important role in the adsorption of CO2. The porous carbon fiber also owned an excellent CO2 reusability, and 96% of the adsorption capacity was maintained after 20 cycles of CO2 adsorption and desorption. The porous carbon fibers enriched with nitrogen could thus be a potential material for CO2 capture. |
| 学科主题 | Science & Technology - Other Topics ; Materials Science |
| 语种 | 英语 |
| 公开日期 | 2018-12-04 |
| 源URL | [http://ir.nimte.ac.cn/handle/174433/17246]  |
| 专题 | 2018专题 |
| 推荐引用方式 GB/T 7714 | Li, De-Hong,Zhang, Yong-Gang,Li, Li,et al. Nitrogen-Enriched Porous Polyacrylonitrile-Based Carbon Fibers for CO2 Capture[J]. INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH,2018,57(34):11608-11616. |
| APA | Li, De-Hong.,Zhang, Yong-Gang.,Li, Li.,Wang, Xue-Fei.,Zhong, Jun-Jun.,...&Song, Shu-Lin.(2018).Nitrogen-Enriched Porous Polyacrylonitrile-Based Carbon Fibers for CO2 Capture.INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH,57(34),11608-11616. |
| MLA | Li, De-Hong,et al."Nitrogen-Enriched Porous Polyacrylonitrile-Based Carbon Fibers for CO2 Capture".INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH 57.34(2018):11608-11616. |
入库方式： OAI收割
来源：宁波材料技术与工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。