Optical and thermal properties of TiO2-doped Y2O3 transparent ceramics synthesized by hot isostatic pressing
文献类型：期刊论文
| 作者 | Li, Xiaokai1,2; Zhu, Qiangqiang1; Xu, Yangyang1,3; Mao, Xiaojian1; Feng, Minghui1; Jiang, Benxue1; Zhang, Long1 |
| 刊名 | Journal of the American Ceramic Society
 |
| 出版日期 | 2018 |
| ISSN号 | 00027820 |
| DOI | 10.1111/jace.16032 |
| 英文摘要 | Highly transparent Y2O3 ceramics using TiO2 as an additive were synthesized by presintering and hot isostatic pressing (HIP). The effects of TiO2 contents and sintering conditions on the optical properties of the final transparent ceramics were investigated. A small amount (0.04-0.16 wt%) may decrease the densification temperature by about 200°C. The Y2O3 ceramics doped with 0.16 wt% TiO2 revealed a transparency of 82% in the wavelength range 1-6 μm. The thermal conductivity of the samples is about 11.8 W/m K at 25°C, which is close to that of the undoped Y2O3 ceramics. © 2018 The American Ceramic Society |
| 出版者 | Blackwell Publishing Inc. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25132]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.Key Laboratory of Materials for High Power Lasers, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Science, Shanghai, China; 2.University of Chinese Academy of Science, Beijing, China; 3.Shanghai University, Shanghai, China |
| 推荐引用方式 GB/T 7714 | Li, Xiaokai,Zhu, Qiangqiang,Xu, Yangyang,et al. Optical and thermal properties of TiO2-doped Y2O3 transparent ceramics synthesized by hot isostatic pressing[J]. Journal of the American Ceramic Society,2018. |
| APA | Li, Xiaokai.,Zhu, Qiangqiang.,Xu, Yangyang.,Mao, Xiaojian.,Feng, Minghui.,...&Zhang, Long.(2018).Optical and thermal properties of TiO2-doped Y2O3 transparent ceramics synthesized by hot isostatic pressing.Journal of the American Ceramic Society. |
| MLA | Li, Xiaokai,et al."Optical and thermal properties of TiO2-doped Y2O3 transparent ceramics synthesized by hot isostatic pressing".Journal of the American Ceramic Society (2018). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。