Effect of gallium ion content on thermal stability and reliability of YAG: Ce phosphor films for white LEDs
文献类型：期刊论文
| 作者 | Liu, Yiming1; Zou, Jun2; Shi, Mingming2; Yang, Bobo2; Han, Ying4; Li, Wenbo3; Wang, Ziming1; Zhou, Heyu1; Li, Mengtian1; Jiang, Nan1 |
| 刊名 | Ceramics International
 |
| 出版日期 | 2018 |
| 卷号 | 44期号:1页码:1091-1098 |
| ISSN号 | 02728842 |
| DOI | 10.1016/j.ceramint.2017.10.056 |
| 英文摘要 | Y2.94(Al1−xGax)5O12:0.06Ce (x = 0.05, 0.1, 0.15, 0.2, 0.25, 0.3) phosphors were prepared by conventional solid-state reaction. Phosphor films are prepared from the synthesized Y2.94(Al1−xGax)5O12:0.06Ce phosphors by a simple spin coating method. The influence of different content of Ga3+doping on the photoluminescence (PL) spectra, thermal stability and reliability of prepared Y2.94(Al1−xGax)5O12:0.06Ce (x = 0.05, 0.1, 0.15, 0.2, 0.25, 0.3) phosphor films were investigated. The emission peak of the Y2.94(Al1−xGax)5O12:0.06Ce (x = 0.05, 0.1, 0.15, 0.2, 0.25, 0.3) phosphor films shifted from 545 nm to 520 nm with the Ga3+content(i.e. the value of x) increasing from 0.05 to 0.3 excited at 460 nm. The phosphor films have excellent thermal stability, and the intensities of PL spectra decrease by about 2%, 5%, 20% and 50% at 373 K, 423 K, 473 K and 523 K, respectively. The xenon lamp aging test show that the relative PL spectra intensity of the phosphor films decreases to 95.55%, 96.24%, 96.05%, 97.67%, 95.96% and 93.22% with the x value is 0.05, 0.1, 0.15, 0.2, 0.25 and 0.3 after the xenon lamp aging test for 168 h. The high temperature and high humidity test show that the relative PL spectra intensity of the phosphor films decreases to 94.36%, 95.6%, 95.26%, 96.87%, 95.28% and 93.1% with the x value is 0.05, 0.1, 0.15, 0.2, 0.25 and 0.3 after the condition of 85 /RH85% for 168 h. The thermal cycling test show that the relative PL spectra intensity of the phosphor films decreases to 90.6%, 91.4%, 93.76%, 94.38%, 91.84% and 88.81% with the x value is 0.05, 0.1, 0.15, 0.2, 0.25 and 0.3 after the condition of 120 for 1 h and −40 for 1 h by turns for eight times. So, it can be generalized that low level of Ga3+doping can enhance the thermal stability and reliability of Y2.94(Al1−xGax)5O12:0.06Ce phosphor films. © 2017 |
| 出版者 | Elsevier Ltd |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25181]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.School of Material Science and Engineering, Shanghai Institute of Technology, Shanghai; 201418, China; 2.School of Science, Shanghai Institute of Technology, Shanghai; 201418, China; 3.Zhejiang Emitting Optoelectronic Technology Co, Ltd., Jiaxing; Zhejiang; 314100, China; 4.Tecore Synchem Optoelectronic Technologies (Tianjin) Co, Ltd., Tianjin; 300451, China |
| 推荐引用方式 GB/T 7714 | Liu, Yiming,Zou, Jun,Shi, Mingming,et al. Effect of gallium ion content on thermal stability and reliability of YAG: Ce phosphor films for white LEDs[J]. Ceramics International,2018,44(1):1091-1098. |
| APA | Liu, Yiming.,Zou, Jun.,Shi, Mingming.,Yang, Bobo.,Han, Ying.,...&Jiang, Nan.(2018).Effect of gallium ion content on thermal stability and reliability of YAG: Ce phosphor films for white LEDs.Ceramics International,44(1),1091-1098. |
| MLA | Liu, Yiming,et al."Effect of gallium ion content on thermal stability and reliability of YAG: Ce phosphor films for white LEDs".Ceramics International 44.1(2018):1091-1098. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。