Influence of composition on molten sulfate-vanadate salt corrosion resistance of lanthanum zirconate coatings
文献类型：期刊论文
| 作者 | Zhu, Changhua1; Yang, Lan1; Zhang, Chengguan1; Yang, Guang1; Chen, Hongfei1; Li, Qian1; Li, Fangzhi2; Gao, Yanfeng1; Liu, Bin1 |
| 刊名 | Ceramics International
 |
| 出版日期 | 2018 |
| ISSN号 | 02728842 |
| DOI | 10.1016/j.ceramint.2018.09.086 |
| 英文摘要 | Three lanthanum zirconate (LZO) thermal barrier coatings with designed La/Zr ratios, i.e., 0.7:1 (LZO-7), 1:1 (LZO-10), and 2:1 (LZO-20), are fabricated by laser enhanced chemical vapor deposition and their corrosion resistance in 40 wt% V2O5 + 60 wt% Na2SO4 mixture is studied at 900 °C. The reaction between lanthanum zirconate coatings and NaVO3 produces LaVO4 and ZrO2, which form impediment layer and prevent deeper penetration of the corrosive sulfate-vanadate molten salt. Meanwhile, no severe transverse cracks are found in all the coatings due to the columnar crystalline microstructures. Furthermore, LZO-20 shows the better corrosion resistance than others as the result of the decreased concentration of corrosive molten salts at the contacting interface, which is attributed to the fact that the excess lanthanum consumes maximum NaVO3. Correspondingly, the LaVO4/ZrO2 ratios rise with the increase of lanthanum content. These results uncover the key role of the lanthanum content on the corrosion resistance of the sulfate-vanadate molten salt and are expected to guide the optimization of the future thermal battier coating design by tailoring the composition. © 2018 Elsevier Ltd and Techna Group S.r.l. |
| 出版者 | Elsevier Ltd |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25220]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.School of Materials Science and Engineering, Shanghai University, Shanghai; 200444, China; 2.Institute of Nuclear Physics and Chemistry, China Academy of Engineering Physics, Mianyang; 621900, China |
| 推荐引用方式 GB/T 7714 | Zhu, Changhua,Yang, Lan,Zhang, Chengguan,et al. Influence of composition on molten sulfate-vanadate salt corrosion resistance of lanthanum zirconate coatings[J]. Ceramics International,2018. |
| APA | Zhu, Changhua.,Yang, Lan.,Zhang, Chengguan.,Yang, Guang.,Chen, Hongfei.,...&Liu, Bin.(2018).Influence of composition on molten sulfate-vanadate salt corrosion resistance of lanthanum zirconate coatings.Ceramics International. |
| MLA | Zhu, Changhua,et al."Influence of composition on molten sulfate-vanadate salt corrosion resistance of lanthanum zirconate coatings".Ceramics International (2018). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。