Fabrication of infrared-transparent 3Y-TZP ceramics with small grain size by pre-sintering in an oxygen atmosphere and hot isostatic pressing
文献类型：期刊论文
| 作者 | Hu, Xu1,2; Jiang, Xiongwei1; Chen, Shuilin1,2; Zhu, Qiangqiang1; Feng, Minghui1; Zhang, Pande1,2; Fan, Jintai1; Jiang, Benxue1; Mao, Xiaojian1; Zhang, Long1 |
| 刊名 | Ceramics International
 |
| 出版日期 | 2018 |
| 卷号 | 44期号:2页码:2093-2097 |
| ISSN号 | 02728842 |
| DOI | 10.1016/j.ceramint.2017.10.158 |
| 英文摘要 | Infrared-transparent 3 mol% tetragonal zirconia polycrystalline (3Y-TZP) ceramics with small grain size were fabricated by pre-sintering in an oxygen atmosphere and hot isostatic pressing (HIP). The microstructure, mechanical, optical, and elevated-temperature properties of the ceramics were investigated. Pre-sintering in an oxygen atmosphere suppressed the grain growth effectively, and the grain size reached approximately 138 nm. The small grain size led to an increased Vickers hardness of 13,790 MPa. The ceramics also exhibited a high transmittance of 76–78% in the range of 3–5 µm. The in-line transmittance remained stable with the temperature elevated to 400 °C. Overall, the results indicated that pre-sintering in an oxygen atmosphere and HIP was an effective method to prepare infrared-transparent 3Y-TZP ceramics with small grain size. © 2017 Elsevier Ltd and Techna Group S.r.l. |
| 出版者 | Elsevier Ltd |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25257]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.Key Laboratory of Materials for High Power Laser, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai; 201800, China; 2.University of Chinese Academy of Sciences, Beijing; 100049, China |
| 推荐引用方式 GB/T 7714 | Hu, Xu,Jiang, Xiongwei,Chen, Shuilin,et al. Fabrication of infrared-transparent 3Y-TZP ceramics with small grain size by pre-sintering in an oxygen atmosphere and hot isostatic pressing[J]. Ceramics International,2018,44(2):2093-2097. |
| APA | Hu, Xu.,Jiang, Xiongwei.,Chen, Shuilin.,Zhu, Qiangqiang.,Feng, Minghui.,...&Zhang, Long.(2018).Fabrication of infrared-transparent 3Y-TZP ceramics with small grain size by pre-sintering in an oxygen atmosphere and hot isostatic pressing.Ceramics International,44(2),2093-2097. |
| MLA | Hu, Xu,et al."Fabrication of infrared-transparent 3Y-TZP ceramics with small grain size by pre-sintering in an oxygen atmosphere and hot isostatic pressing".Ceramics International 44.2(2018):2093-2097. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。