Effects of Ba(Zr0.25Ti0.75)O3 substituent on ferroelectric properties in the BiFeO3-PbTiO3 high temperature ceramics
文献类型：期刊论文
| 作者 | Yu, Zhuo1,2; Zeng, Jiangtao1; Zheng, Liaoying1; Peng, Jiangguli1; Li, Guorong1 |
| 刊名 | Ceramics International
 |
| 出版日期 | 2018 |
| ISSN号 | 02728842 |
| DOI | 10.1016/j.ceramint.2018.08.250 |
| 英文摘要 | (0.75-x)BiFeO3-0.25PbTiO3-xBa(Zr0.25Ti0.75)O3 (BF-PT-BZT) ternary solid solutions were prepared by the solid state reaction method. It was found from X-ray diffraction analysis that the morphotropic phase boundary (MPB) between tetragonal(T) and rhombohedral(R) phases occurred at the composition range of x from 0.13 to 0.28. For BF-PT-base ceramics, the addition of BZT can effectively decreased the tetragonality (c/a) and improved the ferroelectric as well as piezoelectric properties. The maximum value of piezoelectric constant d33 and electromechanical coupling factor kp were 182 pC/N and 0.34, respectively. Also, the ferroelectric transition temperature (Tc) of BF-PT-BZT ceramics varied in the range of 550–298 °C. It is believed that the BF-PT-BZT ternary solid solutions could be a good candidate for high-temperature applications. © 2018 Elsevier Ltd and Techna Group S.r.l. |
| 出版者 | Elsevier Ltd |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25305]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China; 2.University of Chinese Academy of Sciences, Beijing; 100039, China |
| 推荐引用方式 GB/T 7714 | Yu, Zhuo,Zeng, Jiangtao,Zheng, Liaoying,et al. Effects of Ba(Zr0.25Ti0.75)O3 substituent on ferroelectric properties in the BiFeO3-PbTiO3 high temperature ceramics[J]. Ceramics International,2018. |
| APA | Yu, Zhuo,Zeng, Jiangtao,Zheng, Liaoying,Peng, Jiangguli,&Li, Guorong.(2018).Effects of Ba(Zr0.25Ti0.75)O3 substituent on ferroelectric properties in the BiFeO3-PbTiO3 high temperature ceramics.Ceramics International. |
| MLA | Yu, Zhuo,et al."Effects of Ba(Zr0.25Ti0.75)O3 substituent on ferroelectric properties in the BiFeO3-PbTiO3 high temperature ceramics".Ceramics International (2018). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。