Effects of milling time and sintering temperature on structural evolution, densification behavior and properties of a W-20wt.%Cu alloy
文献类型：期刊论文
| 作者 | Li, Chenguang1; Zhou, Yihan1; Xie, Yuehuang1; Zhou, Dengshan2,3; Zhang, Deliang2,3 |
| 刊名 | Journal of Alloys and Compounds
 |
| 出版日期 | 2018 |
| 卷号 | 731页码:537-545 |
| ISSN号 | 09258388 |
| DOI | 10.1016/j.jallcom.2017.10.081 |
| 英文摘要 | The dependence of structural evolution, densification behavior and property changes of a W-20wt.%Cu alloy powder on milling time and sintering temperature were investigated in this study. With the milling time being less than 48 h, the average size, morphology and microstructure of the milled powder particles are strongly influenced by the milling time. But with increasing the milling time from 48 to 96 h, no clear changes are observed other than a distinct decrease in the W lattice parameter. The 48 h milled nanocrystalline alloy powder was chosen to fabricate bulk W-20wt.%Cu samples by vacuum sintering for 2 h at 1050, 1150 and 1250 °C respectively. During sintering at 1150 °C, both the powder particles and W particles in the powder particles undergo rearrangement, making the sample sintered at 1150 °C have the highest relative density, hardness and electrical and thermal conductivities. Due to insufficient solid state diffusion and the formation of large W contiguities as well as Cu pools, the samples sintered at 1050 and 1250 °C, respectively, have lower relative densities in comparison with the sample sintered at 1150 °C. The impurity introduced to the powder particles during milling also affects the densification of the powder compacts and their physical properties. © 2017 Elsevier B.V. |
| 出版者 | Elsevier Ltd |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25310]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.The State Key Laboratory of Metal Matrix Composites, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai; 200240, China; 2.Key Laboratory for Anisotropy and Texture of Materials (Ministry of Education), Northeastern University, Shenyang; 110819, China; 3.Institute of Ceramics and Powder Metallurgy, School of Materials Science and Engineering, Northeastern University, Shenyang; 110819, China |
| 推荐引用方式 GB/T 7714 | Li, Chenguang,Zhou, Yihan,Xie, Yuehuang,et al. Effects of milling time and sintering temperature on structural evolution, densification behavior and properties of a W-20wt.%Cu alloy[J]. Journal of Alloys and Compounds,2018,731:537-545. |
| APA | Li, Chenguang,Zhou, Yihan,Xie, Yuehuang,Zhou, Dengshan,&Zhang, Deliang.(2018).Effects of milling time and sintering temperature on structural evolution, densification behavior and properties of a W-20wt.%Cu alloy.Journal of Alloys and Compounds,731,537-545. |
| MLA | Li, Chenguang,et al."Effects of milling time and sintering temperature on structural evolution, densification behavior and properties of a W-20wt.%Cu alloy".Journal of Alloys and Compounds 731(2018):537-545. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。