Effect of Si4+doping on the microstructure and magneto-optical properties of TAG transparent ceramics
文献类型：期刊论文
| 作者 | Hao, Deming1,2; Shao, Xiuchen1,3; Tang, Yanru1,2; Yi, Xuezhuan1; Chen, Jie1,3; Zhou, Shengming1 |
| 刊名 | Optical Materials
 |
| 出版日期 | 2018 |
| 卷号 | 77页码:253-257 |
| ISSN号 | 09253467 |
| DOI | 10.1016/j.optmat.2018.01.049 |
| 英文摘要 | The Si-doped TAG transparent ceramics were fabricated successfully using solid state reaction and vacuum sintering. Influence of Si4+doping (0-0.6at%) on microstructure and magneto-optical properties of TAG ceramics was investigated. It was found that doping Si4+into TAG was conductive to remove the porosity and improve the optical quality of TAG ceramics significantly. The TAG ceramic sample with 0.2at% Si4+doping (S1) has the highest transmittance among the samples, which can reach 80% in the 1000–1500nm region and it also has the largest grain size of 42.9μm. No pores and impurity phase were found within the grains or along the boundary. The Verdet constant of sample S1 was measured and the value at 633nm was 173.46 rad/Tm, which was similar with that of pure TAG crystal and 29% higher than that of TGG crystal. © 2018 Elsevier B.V. |
| 出版者 | Elsevier B.V. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25328]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.Key Laboratory of Materials for High Power Laser, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai, China; 2.University of Chinese Academy of Sciences, Beijing, China; 3.ShanghaiTech University, Shanghai; 201210, China |
| 推荐引用方式 GB/T 7714 | Hao, Deming,Shao, Xiuchen,Tang, Yanru,et al. Effect of Si4+doping on the microstructure and magneto-optical properties of TAG transparent ceramics[J]. Optical Materials,2018,77:253-257. |
| APA | Hao, Deming,Shao, Xiuchen,Tang, Yanru,Yi, Xuezhuan,Chen, Jie,&Zhou, Shengming.(2018).Effect of Si4+doping on the microstructure and magneto-optical properties of TAG transparent ceramics.Optical Materials,77,253-257. |
| MLA | Hao, Deming,et al."Effect of Si4+doping on the microstructure and magneto-optical properties of TAG transparent ceramics".Optical Materials 77(2018):253-257. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。