High solid loading, low viscosity photosensitive Al2O3 slurry for stereolithography based additive manufacturing
文献类型：期刊论文
| 作者 | Zhang, Keqiang1,2; Xie, Chen1; Wang, Gang3; He, Rujie1,4; Ding, Guojiao1; Wang, Min1; Dai, Dawei5; Fang, Daining1,4 |
| 刊名 | Ceramics International
 |
| 出版日期 | 2018 |
| ISSN号 | 02728842 |
| DOI | 10.1016/j.ceramint.2018.09.152 |
| 英文摘要 | Photosensitive Al2O3-resin slurries with high solid loading, low viscosity used for stereolithography based additive manufacturing were prepared in this paper. The dispersion behavior and rheological behavior of the Al2O3-resin slurries were studied by rheology observation and sedimentation tests. The dispersant type, concentration and solid loading had significant effects on the rheological behavior and stability of the photosensitive Al2O3-resin slurries. A long term stability and homogeneity slurry was obtained when the dispersant and concentration were KOS110 and 5 wt%, respectively. The Al2O3 slurry prepared with a high solid loading up to 60 vol%, low viscosity of 15.4 Pa s at 200 s−1 was chosen for stereolithography based additive manufacturing. © 2018 Elsevier Ltd and Techna Group S.r.l. |
| 出版者 | Elsevier Ltd |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25332]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing; 100081, China; 2.State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing; 100081, China; 3.School of Mechanical and Automotive Engineering, Anhui Polytechnic University, Wuhu; 241000, China; 4.Beijing Key Laboratory of Lightweight Multi-Functional Composite Materials and Structures, Beijing Institute of Technology, Beijing; 100081, China; 5.People's Liberation Army Institute of Neurosurgery, Shanghai Institute of Neurosurgery, Department of Neurosurgery, Changzheng Hospital, Second Military Medical University, Shanghai; 200003, China |
| 推荐引用方式 GB/T 7714 | Zhang, Keqiang,Xie, Chen,Wang, Gang,et al. High solid loading, low viscosity photosensitive Al2O3 slurry for stereolithography based additive manufacturing[J]. Ceramics International,2018. |
| APA | Zhang, Keqiang.,Xie, Chen.,Wang, Gang.,He, Rujie.,Ding, Guojiao.,...&Fang, Daining.(2018).High solid loading, low viscosity photosensitive Al2O3 slurry for stereolithography based additive manufacturing.Ceramics International. |
| MLA | Zhang, Keqiang,et al."High solid loading, low viscosity photosensitive Al2O3 slurry for stereolithography based additive manufacturing".Ceramics International (2018). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。