| 英文摘要 | A CaF2CeF3disordered crystal containing 1.06% of Er3+ions was grown by the temperature gradient technique. Optical absorption and emission spectra recorded at room temperature and at 10 K, luminescence decay curve recorded at room temperature, and extended x-ray-absorption fine structure spectra were analyzed with an intention to assess the laser potential related to the4I13/2→4I15/2transition of Er3+. In addition, the thermal diffusivity of the crystal was measured at room temperature. The analysis of room-temperature spectra revealed that the 4I13/2 emission is long-lived with a radiative lifetime value of 5.5 ms, peak emission cross section of 0.737times;10-20cm2, and large spectral width pointing at the tunability of the emission wavelength in the region stretching from approximately 1480 nm to 1630 nm. The energies of the crystal field components for the ground and excited multiplets determined from low-temperature absorption and emission spectra made it possible to predict successfully the spectral position and shape of the room-temperature4I13/2→4I15/2emission band. Based on the correlation of the optical spectra and dynamics of the luminescence decay, it was concluded that in contrast to Yb3+ions in heavily doped CaF2erbium ions in the CaF2-CeF3crystal reside in numerous sites with dissimilar relaxation rates. © 2017 Chinese Physical Society and IOP Publishing Ltd. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25442]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.School of Physics Science and Engineering, Institute for Advanced Study, Tongji University, Shanghai; 200092, China; 2.Shanghai Engineering Research Center for Sapphire Crystals, Shanghai; 201899, China; 3.Key Laboratory of Transparent and Opto-Functional Advanced Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 201800, China; 4.School of Materials Science and Engineering, Tongji University, Shanghai; 200092, China; 5.Jiangsu Key Laboratory of Advanced Laser Materials and Devices, School of Physics and Electronic Engineering, Jiangsu Normal University, Xuzhou; 221116, China; 6.Institute of Low Temperature and Structure Research, Polish Academy of Sciences (ILTSR), Okólna, Wroclaw; 50-422, Poland |
| 推荐引用方式 GB/T 7714 | Wang, Qing-Guo,Su, Liangbi,Liu, Jun-Fang,et al. Intensities and spectral features of the[J]. Chinese Physics B,2017,26(11). |
| APA | Wang, Qing-Guo.,Su, Liangbi.,Liu, Jun-Fang.,Liu, Bin.,Wu, Feng.,...&Xu, Jun.(2017).Intensities and spectral features of the.Chinese Physics B,26(11). |
| MLA | Wang, Qing-Guo,et al."Intensities and spectral features of the".Chinese Physics B 26.11(2017). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。