Fabrication and luminescent properties of highly transparent Er3Al5O12ceramics
文献类型：期刊论文
| 作者 | Hu, Song1,2,3; Qin, Xianpeng1; Liu, Xiaoxia2,3; Zhou, Guohong1; Lu, Chunhua2,3; Wang, Shiwei1; Xu, Zhongzi2,3 |
| 刊名 | Optical Materials
 |
| 出版日期 | 2017 |
| 卷号 | 71页码:86-89 |
| ISSN号 | 09253467 |
| DOI | 10.1016/j.optmat.2016.05.018 |
| 英文摘要 | Highly transparent Er3Al5O12(ErAG) ceramic was fabricated by a solid-state reactive sintering method under vacuum. The optical property, microstructure and up-conversion luminescence of the ErAG ceramic were investigated. For the 3 mm thick sample, the in-line transmittance at the wavelength of 3000 nm and 425 nm were about 84% and 81%, respectively, which was very close to the theoretical transmittance of the Er3Al5O12single crystal. Micrograph of the ErAG transparent ceramic exhibited a pore-free structure and the density of the ceramic was measured to be 6.38 g/cm3. Average grain size of the ceramic was about 9 μm. When pumped by a 980 nm laser diodes (LD), strong green and red emission in the ErAG ceramic was observed from the photoluminescence (PL) spectrum. The luminescent properties of the ceramic under the excitation of LD with various pumping power were investigated. © 2016 Elsevier B.V. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25470]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China; 2.State Key Laboratory of Materials-Orient Chemical Engineering, College of Materials Science and Engineering, Nanjing Tech University, Nanjing; 210009, China; 3.Jiangsu Collaborative Innovation Center for Advanced Inorganic Function Composites, Nanjing Tech University, Nanjing; 210009, China |
| 推荐引用方式 GB/T 7714 | Hu, Song,Qin, Xianpeng,Liu, Xiaoxia,et al. Fabrication and luminescent properties of highly transparent Er3Al5O12ceramics[J]. Optical Materials,2017,71:86-89. |
| APA | Hu, Song.,Qin, Xianpeng.,Liu, Xiaoxia.,Zhou, Guohong.,Lu, Chunhua.,...&Xu, Zhongzi.(2017).Fabrication and luminescent properties of highly transparent Er3Al5O12ceramics.Optical Materials,71,86-89. |
| MLA | Hu, Song,et al."Fabrication and luminescent properties of highly transparent Er3Al5O12ceramics".Optical Materials 71(2017):86-89. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。