Preparation and characterization of SO3-doped barium borosilicate glass-ceramics containing zirconolite and barite phases
文献类型：期刊论文
| 作者 | Wang, Xin1; Wu, Lang1; Li, Huidong2; Xiao, Jizong1; Cai, Xin1; Teng, Yuancheng1 |
| 刊名 | Ceramics International
 |
| 出版日期 | 2017 |
| 卷号 | 43期号:1页码:534-539 |
| ISSN号 | 02728842 |
| DOI | 10.1016/j.ceramint.2016.09.190 |
| 英文摘要 | In order to improve the solubility of actinides and sulfate in the glass matrix, barium borosilicate glass-ceramics containing zirconolite and barite crystalline phases were developed. The effects of SO3addition (0–8 wt%) on crystalline phases, microstructure, and chemical durability of glass-ceramics belonging to SiO2-B2O3-Na2O-BaO-CaO-TiO2-ZrO2-Nd2O3-SO3system were mainly studied. The results show that glass transformation temperature decreases slightly with increasing SO3content. The main crystalline phase is zirconolite for all of the samples. When the addition SO3content is higher or equal to 4 wt%, rice-shaped barite crystals appear in the bulk of glass-ceramics. Barite phase was formed during the melting stage. X-ray fluorescence analysis indicates that about 1.3 wt% of SO3can be incorporated in the glass-ceramics when the addition content of SO3is 6 wt%. S element mainly distributes in the barite crystals. The decomposition of sulfate mainly occurs during the melting process. Moreover, the addition of a certain content (≤6 wt%) of sulfate has no significant influence on the chemical durability of barium borosilicate glass-ceramics. © 2016 Elsevier Ltd and Techna Group S.r.l. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25514]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials, Southwest University of Science and Technology, Mianyang; 621010, China; 2.Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China |
| 推荐引用方式 GB/T 7714 | Wang, Xin,Wu, Lang,Li, Huidong,et al. Preparation and characterization of SO3-doped barium borosilicate glass-ceramics containing zirconolite and barite phases[J]. Ceramics International,2017,43(1):534-539. |
| APA | Wang, Xin,Wu, Lang,Li, Huidong,Xiao, Jizong,Cai, Xin,&Teng, Yuancheng.(2017).Preparation and characterization of SO3-doped barium borosilicate glass-ceramics containing zirconolite and barite phases.Ceramics International,43(1),534-539. |
| MLA | Wang, Xin,et al."Preparation and characterization of SO3-doped barium borosilicate glass-ceramics containing zirconolite and barite phases".Ceramics International 43.1(2017):534-539. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。