Elaboration of translucent ZnO ceramics by spark plasma sintering under low temperature
文献类型：期刊论文
| 作者 | Lin, Debao1; Fan, Lingcong1; Shi, Ying1; Xie, Jianjun1; Lei, Fang1; Ren, Dudi2 |
| 刊名 | Optical Materials
 |
| 出版日期 | 2017 |
| 卷号 | 71页码:151-156 |
| ISSN号 | 09253467 |
| DOI | 10.1016/j.optmat.2016.06.018 |
| 英文摘要 | ZnO is considered to be a potential ultrafast scintillator. In this work, nanosized ZnO powders were synthesized via thermal decomposition of precursors prepared by indirect-precipitation method from zinc nitrate and urea in aqueous solutions. The resultant single phased ZnO powder calcined at 600 °C for 2 h had a primary grain size of 66.0 nm with good dispersity showing excellent sinterability. Translucent ZnO ceramic with a relative density of 99.2% was fabricated successfully by spark plasma sintering at 850 °C for 10 min under the pressure of 80 MPa. The obtained ZnO ceramic exhibited fully dense and homogenous microstructure with average grain size of ∼1 μm, leading to an in-line optical transmission of 11.8% at a wavelength of 950 nm. © 2016 Elsevier B.V. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25547]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.School of Materials Science and Engineering, Shanghai University, Shanghai; 200444, China; 2.Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China |
| 推荐引用方式 GB/T 7714 | Lin, Debao,Fan, Lingcong,Shi, Ying,et al. Elaboration of translucent ZnO ceramics by spark plasma sintering under low temperature[J]. Optical Materials,2017,71:151-156. |
| APA | Lin, Debao,Fan, Lingcong,Shi, Ying,Xie, Jianjun,Lei, Fang,&Ren, Dudi.(2017).Elaboration of translucent ZnO ceramics by spark plasma sintering under low temperature.Optical Materials,71,151-156. |
| MLA | Lin, Debao,et al."Elaboration of translucent ZnO ceramics by spark plasma sintering under low temperature".Optical Materials 71(2017):151-156. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。