Solution casting Nafion/polytetrafluoroethylene membrane for vanadium redox flow battery application
文献类型：期刊论文
| 作者 | Teng, Xiangguo1; Sun, Cui1,2; Dai, Jicui1; Liu, Haiping1; Su, Jing1; Li, Faqiang3 |
| 刊名 | ELECTROCHIMICA ACTA
 |
| 出版日期 | 2013-01-15 |
| 卷号 | 88页码:725-734 |
| 关键词 | Vanadium Redox Flow Battery Nafion Polytetrafluoroethylene Casting Membrane |
| 文献子类 | Article |
| 英文摘要 | Solution casting method was adopted using Nafion and polytetrafluoroethylene (PTFE) solution to prepare Nafion/PTFE blend membranes for vanadium redox flow battery application. The physicochemical properties of the membranes were characterized by using water uptake, Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) and thermal analysis (TA). The electrochemical properties of the membranes were examined by using electrochemical impedance spectroscopy (EIS) and single cell test. Despite the high miscibility of PTFE with Nafion, the addition of hydrophobic PTFE reduces the water uptake, ion exchange capacity (IEC) and conductivity of blend membranes. But PTFE can increase the crystallinity, thermal stability of Nafion/PTFE membranes and reduce the vanadium permeability. The blend membrane with PTFE (30 wt%, N0.7P0.3) was chosen and investigated for VRB single cell test. The energy efficiency of this VRB with N0.7P0.3 membrane was 85.1% at current density of 50 mA cm(-2), which was superior to that of recast Nafion (r-Nafion) membrane (80.5%). Self-discharge test shows that the decay of open circuit potential of N0.7P0.3 membrane is much lower than that of r-Nafion membrane. More than 50 cycles charge-discharge test proved that the N0.7P0.3 membrane possesses high stability in long time running. Chemical stabilities of the chosen N0.7P0.3 membrane are further proved by soaking the membrane for 3 weeks in highly oxidative V(V) solution. All results suggest that the addition of PTFE is a simple and effective way to improve the performance of Nafion for VRB application. (C) 2012 Elsevier Ltd. All rights reserved. |
| WOS关键词 | POLYMER ELECTROLYTE MEMBRANES ; PROTON-EXCHANGE MEMBRANES ; FUEL-CELL APPLICATIONS ; NAFION/PTFE COMPOSITE MEMBRANES ; HYBRID MEMBRANE ; PERFORMANCE ; DIFFUSION ; BEHAVIOR ; ACID ; PTFE |
| WOS研究方向 | Electrochemistry |
| 语种 | 英语 |
| WOS记录号 | WOS:000315076300097 |
| 源URL | [http://ir.isl.ac.cn/handle/363002/4435]  |
| 专题 | 青海盐湖研究所_青海盐湖研究所知识仓储 |
| 作者单位 | 1.Harbin Inst Technol Weihai, Sch Marine Sci & Technol, Weihai 264209, Peoples R China 2.Harbin Inst Technol, Dept Appl Chem, Harbin 150001, Peoples R China 3.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China |
| 推荐引用方式 GB/T 7714 | Teng, Xiangguo,Sun, Cui,Dai, Jicui,et al. Solution casting Nafion/polytetrafluoroethylene membrane for vanadium redox flow battery application[J]. ELECTROCHIMICA ACTA,2013,88:725-734. |
| APA | Teng, Xiangguo,Sun, Cui,Dai, Jicui,Liu, Haiping,Su, Jing,&Li, Faqiang.(2013).Solution casting Nafion/polytetrafluoroethylene membrane for vanadium redox flow battery application.ELECTROCHIMICA ACTA,88,725-734. |
| MLA | Teng, Xiangguo,et al."Solution casting Nafion/polytetrafluoroethylene membrane for vanadium redox flow battery application".ELECTROCHIMICA ACTA 88(2013):725-734. |
入库方式： OAI收割
来源：青海盐湖研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。