Investigation and Preparation of High Active Nano-MgO Thin Spherical Material
文献类型：期刊论文
| 作者 | Ren, Xiufeng1; Zhou, Yuan1; Sun, Qingguo1; Nian, Hongen1; Li, Xiang1,2; Cao, Meng Meng1,2 |
| 刊名 | INTEGRATED FERROELECTRICS
 |
| 出版日期 | 2012 |
| 卷号 | 138页码:128-136 |
| 关键词 | High-temperature Spray Mgo Thin Sphere Nano-structure Bet Surface Area |
| 文献子类 | Article |
| 英文摘要 | High active MgO precursor was prepared by high-temperature spray thermal decomposition method using saturated MgCl2 as raw materials. And high active nano-MgO thin spherical materials were prepared by MgO precursor being calcined at different temperatures after multiple hydration, purification, and filtration. The XRD, TG, DSC and SEM were employed to characterize the phase structure and micro-morphology of spherical materials whose formation mechanism was researched. And its activity (average pore size and surface area) was detected by using BET-BJH of N-2 adsorption to get the optimum calcination temperature. The results showed that high active nano-MgO thin spherical material was periclase structure, its surface of nano-flake or rod-like, and thin sphere with diameter of 30 similar to 100 nm and aperture of 10 similar to 60 nm. The aperture was decreased while the surface area, microporous volume and surface activity were increased with preparation process were optimized, for example, calcination temperatures. Nano-MgO thin spherical material with a purity of 99.2 wt% was obtained at 900 degrees C. And BET surface area of nano-sphere reached a maximum value of 31.6 m(2)/g with nest-like structure of particle uniform dispersion and average aperture of 11.2 nm. Meanwhile, the maximum absorption of N-2 was gotten. |
| WOS关键词 | MAGNESIUM-HYDROXIDE ; NANOCRYSTALLINE MGO ; OXIDE ; FABRICATION ; POWDERS ; SIZE |
| WOS研究方向 | Engineering ; Physics |
| 语种 | 英语 |
| WOS记录号 | WOS:000305254500021 |
| 源URL | [http://ir.isl.ac.cn/handle/363002/5551]  |
| 专题 | 青海盐湖研究所_青海盐湖研究所知识仓储 中国科学院青海盐湖研究所 |
| 作者单位 | 1.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Ren, Xiufeng,Zhou, Yuan,Sun, Qingguo,et al. Investigation and Preparation of High Active Nano-MgO Thin Spherical Material[J]. INTEGRATED FERROELECTRICS,2012,138:128-136. |
| APA | Ren, Xiufeng,Zhou, Yuan,Sun, Qingguo,Nian, Hongen,Li, Xiang,&Cao, Meng Meng.(2012).Investigation and Preparation of High Active Nano-MgO Thin Spherical Material.INTEGRATED FERROELECTRICS,138,128-136. |
| MLA | Ren, Xiufeng,et al."Investigation and Preparation of High Active Nano-MgO Thin Spherical Material".INTEGRATED FERROELECTRICS 138(2012):128-136. |
入库方式： OAI收割
来源：青海盐湖研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。