Technology of preparing anode films and the effect of co-sensitization in dye-sensitized solar cells
文献类型：期刊论文
| 作者 | Zhang, Jingchang1,2; Fu, Zhenhai1,3 ; Iv, Qian2; Yang, Xiuying2; Cao, Weiliang1,2
|
| 刊名 | JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY
 |
| 出版日期 | 2012-09-01 |
| 卷号 | 63期号:3页码:554-562 |
| 关键词 | N-zn/tio2 Anode Films Ticl4 Treatment Co-sensitization Dye-sensitized Solar Cell |
| 文献子类 | Article |
| 英文摘要 | Nanocrystalline N-Zn/TiO2 anode films were prepared by doping element N and Zn. These element-doped films have a better performance in dye-sensitized solar cell than the non-doped film. The test shows that the best thickness of N-Zn/TiO2 anode film is 13.5 mu m. UV-Visible measurements show that there is a complementarity in ultraviolet-visible absorbance range between P3OT and N719, both are used as dyes in this study, the former is prepared and the latter is commercially available. SEM shows a significant mass increase of anode film after treated with TiCl4. Solar cells based on N-Zn/TiO2 anode film with TiCl4 treatment was firstly co-sensitized by N719/P3OT. A solar-to-electric energy conversion efficiency of 3.54 % was obtained. Compared with the traditional dye-sensitized solar cell, the photoelectric conversion efficiency, V (oc) and J (sc) have been increased. |
| WOS关键词 | RAY PHOTOELECTRON-SPECTROSCOPY ; TIO2 FILMS ; ZNO FILMS ; EFFICIENCY ; ELECTRODE |
| WOS研究方向 | Materials Science |
| 语种 | 英语 |
| WOS记录号 | WOS:000310162700030 |
| 源URL | [http://ir.isl.ac.cn/handle/363002/5637]  |
| 专题 | 青海盐湖研究所_青海盐湖研究所知识仓储 青海盐湖研究所_盐湖资源与化学实验室 中国科学院青海盐湖研究所 |
| 作者单位 | 1.Beijing Univ Chem Technol, Inst Modern Catalysis, State Key Lab Chem Resource Engn, Beijing 100029, Peoples R China 2.Hainan Inst Sci & Technol, Haikou 571126, Peoples R China 3.Chinese Acad Sci, Qinghai Inst Salt Lakes, Xining 810008, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhang, Jingchang,Fu, Zhenhai,Iv, Qian,et al. Technology of preparing anode films and the effect of co-sensitization in dye-sensitized solar cells[J]. JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY,2012,63(3):554-562. |
| APA | Zhang, Jingchang,Fu, Zhenhai,Iv, Qian,Yang, Xiuying,&Cao, Weiliang.(2012).Technology of preparing anode films and the effect of co-sensitization in dye-sensitized solar cells.JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY,63(3),554-562. |
| MLA | Zhang, Jingchang,et al."Technology of preparing anode films and the effect of co-sensitization in dye-sensitized solar cells".JOURNAL OF SOL-GEL SCIENCE AND TECHNOLOGY 63.3(2012):554-562. |
入库方式： OAI收割
来源：青海盐湖研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。