Fabrication of Yb:Sc2O3laser ceramics by vacuum sintering co-precipitated nano-powders
文献类型：期刊论文
| 作者 | Liu, Qiang1; Dai, Zhengfa1,2; Hreniak, Dariusz3; Li, Shanshan2; Liu, Wenbin4; Wang, Wei2; Luo, Wei2; Li, Chaoyu2; Dai, Jiawei2; Chen, Haohong2 |
| 刊名 | Optical Materials
 |
| 出版日期 | 2017 |
| 卷号 | 72页码:482-490 |
| ISSN号 | 09253467 |
| DOI | 10.1016/j.optmat.2017.05.057 |
| 英文摘要 | Ytterbium doped scandium oxide (Yb:Sc2O3) nano-powders were synthesized by a co-precipitation method. Ammonium hydrogen carbonate (NH4HCO3) and ammonia sulfate ((NH4)2SO4) were used in the precipitation process as the precipitant and dispersing agent, respectively. Structural properties and morphology of the precursor and nano-powders were investigated by BET, XRD, and SEM measurements. Ultra-fine and low agglomerated 5 at%Yb:Sc2O3powders with the average particle size of 86 nm were obtained after calcination of the precipitate at 1100 °C for 5 h, that was found to be the optimal temperature for preparation of 5 at%Sc2O3powders for further sintering. 5 at%Yb:Sc2O3transparent ceramics with in-line transmittance of 73.9% at 1100 nm and average grain size of 182 μm were fabricated by vacuum sintering of the optimal powder at 1850 °C for 10 h. The microstructure, the spectroscopic properties and the gain characteristics of obtained 5 at%Yb:Sc2O3ceramics were also studied and discussed. © 2017 |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25945]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.School of Material Science and Engineering, Jiangsu University, Zhenjiang; 212013, China; 2.Key Laboratory of Transparent and Opto-functional Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China; 3.Department of Excited State Spectroscopy, Institute of Low Temperature and Structure Research, Polish Academy of Sciences, Wroclaw; 50-422, Poland; 4.Shanghai Key Laboratory of Crime Scene Evidence, Shanghai Research Institute of Criminal Science and Technology, Shanghai; 200083, China; 5.Department of Physics, Shanghai Normal University, Shanghai; 200234, China |
| 推荐引用方式 GB/T 7714 | Liu, Qiang,Dai, Zhengfa,Hreniak, Dariusz,et al. Fabrication of Yb:Sc2O3laser ceramics by vacuum sintering co-precipitated nano-powders[J]. Optical Materials,2017,72:482-490. |
| APA | Liu, Qiang.,Dai, Zhengfa.,Hreniak, Dariusz.,Li, Shanshan.,Liu, Wenbin.,...&Li, Jiang.(2017).Fabrication of Yb:Sc2O3laser ceramics by vacuum sintering co-precipitated nano-powders.Optical Materials,72,482-490. |
| MLA | Liu, Qiang,et al."Fabrication of Yb:Sc2O3laser ceramics by vacuum sintering co-precipitated nano-powders".Optical Materials 72(2017):482-490. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。