Fabrication and properties of (TbxY1−x)3Al5O12transparent ceramics by hot isostatic pressing
文献类型：期刊论文
| 作者 | Duan, Pingping1; Liu, Peng2; Xu, Xiaodong2; Wang, Wei1; Wan, Zhong1; Zhang, Shouyi2; Wang, Yinzhen1; Zhang, Jian3 |
| 刊名 | Optical Materials
 |
| 出版日期 | 2017 |
| 卷号 | 72页码:58-62 |
| ISSN号 | 09253467 |
| DOI | 10.1016/j.optmat.2017.05.035 |
| 英文摘要 | (TbxY1−x)3Al5O12(x = 0.2, 0.5, 0.8) transparent ceramics were synthesized by a solid-state reaction and HIP. All the samples were pre-sintered at 1650 °C for 4 h in a muffle and later HIPed at 1650 °C for 3 h. (Tb0.2Y0.8)3Al5O12transparent ceramics exhibit best microstructure with an average grain size of approximately 5.22 μm and optical transmittance of over 65% in the region of 500–1600 nm. Additionally, average grain sizes of all the samples are less than 10 μm. XRD scanning patterns indicate that only the (Tb0.8Y0.2)3Al5O12samples have little secondary phases. © 2017 Elsevier B.V. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25931]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.Guangdong Engineering Technology Research Center of Efficient Green Energy and Environmental Protection Materials, Guangdong Key Laboratory of Quantum Engineering and Quantum Materials, School of Physics& Telecommunication Engineering, South China Normal University, Guangzhou; 510006, China; 2.Jiangsu Key Laboratory of Advanced Laser Materials and Devices, School of Physics& Electronic Engineering, Jiangsu Normal University, Xuzhou; 221116, China; 3.Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China |
| 推荐引用方式 GB/T 7714 | Duan, Pingping,Liu, Peng,Xu, Xiaodong,et al. Fabrication and properties of (TbxY1−x)3Al5O12transparent ceramics by hot isostatic pressing[J]. Optical Materials,2017,72:58-62. |
| APA | Duan, Pingping.,Liu, Peng.,Xu, Xiaodong.,Wang, Wei.,Wan, Zhong.,...&Zhang, Jian.(2017).Fabrication and properties of (TbxY1−x)3Al5O12transparent ceramics by hot isostatic pressing.Optical Materials,72,58-62. |
| MLA | Duan, Pingping,et al."Fabrication and properties of (TbxY1−x)3Al5O12transparent ceramics by hot isostatic pressing".Optical Materials 72(2017):58-62. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。