Relationship between cracks and microstructures in APS YSZ coatings at elevated temperatures
文献类型：期刊论文
| 作者 | Song, Xuemei1; Meng, Fangli1; Kong, Mingguang2; Liu, Ziwei1; Huang, Liping3; Zheng, Xuebin3; Zeng, Yi1,4 |
| 刊名 | Materials Characterization
 |
| 出版日期 | 2017 |
| 卷号 | 131页码:277-284 |
| ISSN号 | 10445803 |
| DOI | 10.1016/j.matchar.2017.07.008 |
| 英文摘要 | Yttria-stabilized zirconia (YSZ) thermal barrier coatings (TBCs) were prepared by plasma spraying. Thermally grown oxide (TGO) was formed between the YSZ layer and the bond coat during heat treatment of the YSZ TBCs. The generation and extension behavior of cracks before and after heat treatment were characterized by scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD) combined with 3D reconstruction technology. The characterization results give a direct evidence that the generation and extension of cracks is closely related to other microstructures such as columnar grains, TGO morphology, TGO composition, and TGO orientation. For example, large interlaminar cracks in as-sprayed YSZ coatings often appeared along with columnar grains, which can be explained by their similar formation conditions. The formation of new cracks such as vertical cracks, plane cracks and other cracks along the TGO grain boundary after heat treatment often resulted from TGO growth stresses. Therefore, the generation and extension of cracks can be controlled by regulating the formation of columnar grains and TGO. © 2017 Elsevier Inc. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25901]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.The State Key Lab of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China; 2.Key Laboratory of Materials Physics, Institute of Solid State Physics, Chinese Academy of Sciences, Hefei; 230031, China; 3.Key Laboratory of Inorganic Coating Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China; 4.CAS Center for Excellence in Superconducting Electronics (CENSE), Shanghai; 200050, China |
| 推荐引用方式 GB/T 7714 | Song, Xuemei,Meng, Fangli,Kong, Mingguang,et al. Relationship between cracks and microstructures in APS YSZ coatings at elevated temperatures[J]. Materials Characterization,2017,131:277-284. |
| APA | Song, Xuemei.,Meng, Fangli.,Kong, Mingguang.,Liu, Ziwei.,Huang, Liping.,...&Zeng, Yi.(2017).Relationship between cracks and microstructures in APS YSZ coatings at elevated temperatures.Materials Characterization,131,277-284. |
| MLA | Song, Xuemei,et al."Relationship between cracks and microstructures in APS YSZ coatings at elevated temperatures".Materials Characterization 131(2017):277-284. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。