Annealing effects on the microstructure and magnetic properties of Y3Fe5O12films deposited on Si/SiO2substrates by RF magnetron sputtering
文献类型：期刊论文
| 作者 | Lian, Jianyun1,2; Chen, Ying1; Liu, Zhen1; Zhu, Mingkang1; Wang, Genshui1; Zhang, Wenbin1; Dong, Xianlin1 |
| 刊名 | Ceramics International
 |
| 出版日期 | 2017 |
| 卷号 | 43期号:10页码:7477-7481 |
| ISSN号 | 02728842 |
| DOI | 10.1016/j.ceramint.2017.03.023 |
| 英文摘要 | Crack-free Yttrium iron garnet (Y3Fe5O12, YIG) thin films were successfully deposited on Si/SiO2substrates by RF magnetron sputtering, through controlling the annealing temperature and cooling rate during post-annealing process. The annealing condition dependences of crystallinity, microstructures and magnetic properties of YIG films were investigated. With the increase of the annealing temperature, the saturation magnetization of YIG films increases and the coercive field decreases, while the ferromagnetic resonance (FMR) linewidth becomes wider. The films annealed at 750 °C with cooling rate of 1 °C/min are crack-free and present excellent comprehensive performances, the corresponding coercive field is 32 Oe and the FMR linewidth is 57 Oe at 9.4 GHz. These results indicate that high-quality crack-free YIG films with excellent magnetic properties can be achieved on Si/SiO2substrates by controlling the annealing process, which makes it more convenient to fabricate low-loss microwave integrated devices. © 2017 Elsevier Ltd and Techna Group S.r.l. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25809]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai; 200050, China; 2.University of Chinese Academy of Sciences, Beijing; 100049, China |
| 推荐引用方式 GB/T 7714 | Lian, Jianyun,Chen, Ying,Liu, Zhen,et al. Annealing effects on the microstructure and magnetic properties of Y3Fe5O12films deposited on Si/SiO2substrates by RF magnetron sputtering[J]. Ceramics International,2017,43(10):7477-7481. |
| APA | Lian, Jianyun.,Chen, Ying.,Liu, Zhen.,Zhu, Mingkang.,Wang, Genshui.,...&Dong, Xianlin.(2017).Annealing effects on the microstructure and magnetic properties of Y3Fe5O12films deposited on Si/SiO2substrates by RF magnetron sputtering.Ceramics International,43(10),7477-7481. |
| MLA | Lian, Jianyun,et al."Annealing effects on the microstructure and magnetic properties of Y3Fe5O12films deposited on Si/SiO2substrates by RF magnetron sputtering".Ceramics International 43.10(2017):7477-7481. |