Induced anisotropic behavior and enhanced electrical properties on hot-pressed strontium barium niobate ceramics
文献类型：期刊论文
| 作者 | Chen, Hui1,2; Guo, Shaobo1; Yao, Chunhua1; Dong, Xianlin1; Mao, Chaoliang1; Wang, Genshui1 |
| 刊名 | Ceramics International
 |
| 出版日期 | 2017 |
| 卷号 | 43期号:4页码:3610-3615 |
| ISSN号 | 02728842 |
| DOI | 10.1016/j.ceramint.2016.11.198 |
| 英文摘要 | Sr0.30Ba0.70Nb2O6(SBN30) ferroelectric ceramics were fabricated by conventional sintering (CS) and by hot-pressing sintering (HP) and their crystal structure, microstructure, dielectric, ferroelectric and pyroelectric properties were studied and compared. Preferred orientation of the HP ceramics was detected through X-ray diffraction. Dense microstructure virtually free of pores has been achieved in HP samples. Moreover, the HP samples manifested prominent anisotropy in electrical properties. Besides, the relative permittivity (Εr), saturated polarization (Ps), pyroelectric coefficient (p) in the direction perpendicular to the pressing axis were much higher than those of the randomly oriented CS samples. The HP samples sintered under 200 MPa show excellent pyroelectric properties in the direction perpendicular to the pressing axis, with pyroelectric coefficient of 2.38×10−8C/cm2K and pyroelectric figure of merit of Fi=1.13 pm/V, Fv=1.89 m2/C and Fd=0.63 μPa−1/2which roughly triple the values obtained in CS samples. These results indicate that hot-pressing is a viable option for accessing single-crystal-like anisotropy as well as enhanced electrical properties in polycrystalline ceramics, thus unveiling the distinctive potential of HP SBN30 ceramics for infrared detector applications. © 2016 Elsevier Ltd and Techna Group S.r.l. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25735]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.Key Laboratory of Inorganic Functional Materials and Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai; 200050, China; 2.University of Chinese Academy of Sciences, Beijing; 100049, China |
| 推荐引用方式 GB/T 7714 | Chen, Hui,Guo, Shaobo,Yao, Chunhua,et al. Induced anisotropic behavior and enhanced electrical properties on hot-pressed strontium barium niobate ceramics[J]. Ceramics International,2017,43(4):3610-3615. |
| APA | Chen, Hui,Guo, Shaobo,Yao, Chunhua,Dong, Xianlin,Mao, Chaoliang,&Wang, Genshui.(2017).Induced anisotropic behavior and enhanced electrical properties on hot-pressed strontium barium niobate ceramics.Ceramics International,43(4),3610-3615. |
| MLA | Chen, Hui,et al."Induced anisotropic behavior and enhanced electrical properties on hot-pressed strontium barium niobate ceramics".Ceramics International 43.4(2017):3610-3615. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。