Mesoporous bioactive glass functionalized 3D Ti-6Al-4V Scaffolds with improved surface bioactivity
文献类型：期刊论文
| 作者 | Ye, Xiaotong1,2; Leeflang, Sander3; Wu, Chengtie1; Chang, Jiang1; Zhou, Jie3; Huan, Zhiguang1 |
| 刊名 | Materials
 |
| 出版日期 | 2017 |
| 卷号 | 10期号:11 |
| DOI | 10.3390/ma10111244 |
| 英文摘要 | Porous Ti-6Al-4V scaffolds fabricated by means of selective laser melting (SLM), having controllable geometrical features and preferable mechanical properties, have been developed as a class of biomaterials that hold promising potential for bone repair. However, the inherent bio-inertness of the Ti-6Al-4V alloy as the matrix of the scaffolds results in a lack in the ability to stimulate bone ingrowth and regeneration. The aim of the present study was to develop a bioactive coating on the struts of SLM Ti-6Al-4V scaffolds in order to add the desired surface osteogenesis ability. Mesoporous bioactive glasses (MBGs) coating was applied on the strut surfaces of the SLM Ti-6Al-4V scaffolds through spin coating, followed by a heat treatment. It was found that the coating could maintain the characteristic mesoporous structure and chemical composition of MBG, and establish good interfacial adhesion to the Ti-6Al-4V substrate. The compressive strength and pore interconnectivity of the scaffolds were not affected by the coating. Moreover, the results obtained from in vitro cell culture experiments demonstrated that the attachment, proliferation, and differentiation of human bone marrow stromal cells (hBMSCs) on the MBG-coated Ti-6Al-4V scaffolds were improved as compared with those on the conventional bioactive glass (BG)-coated Ti-6Al-4V scaffolds and bare-metal Ti-6Al-4V scaffolds. Our results demonstrated that the MBG coating by using the spinning coating method could be an effective approach to achieving enhanced surface biofunctionalization for SLM Ti-6Al-4V scaffolds. © 2017 by the authors. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25706]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai; 200050, China; 2.University of Chinese Academy of Sciences, No.19(A), Yuquan Road, Shijingshan District, Beijing; 100049, China; 3.Department of Biomechanical Engineering, Delft University of Technology, Mekelweg 2, Delft; 2628 CD, Netherlands |
| 推荐引用方式 GB/T 7714 | Ye, Xiaotong,Leeflang, Sander,Wu, Chengtie,et al. Mesoporous bioactive glass functionalized 3D Ti-6Al-4V Scaffolds with improved surface bioactivity[J]. Materials,2017,10(11). |
| APA | Ye, Xiaotong,Leeflang, Sander,Wu, Chengtie,Chang, Jiang,Zhou, Jie,&Huan, Zhiguang.(2017).Mesoporous bioactive glass functionalized 3D Ti-6Al-4V Scaffolds with improved surface bioactivity.Materials,10(11). |
| MLA | Ye, Xiaotong,et al."Mesoporous bioactive glass functionalized 3D Ti-6Al-4V Scaffolds with improved surface bioactivity".Materials 10.11(2017). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。