Abnormal bipolar resistive switching behavior in carbon-iron composite films with different thicknesses
文献类型：期刊论文
| 作者 | Zhou, J.W.1; Li, T.R.1; Zhang, D.1; Ren, B.1; Zhang, S.W.1; Huang, J.1; Zhang, J.M.3; Wang, L.1; Jiang, Y.C.2; Gao, J.2 |
| 刊名 | Vacuum
 |
| 出版日期 | 2017 |
| 卷号 | 135页码:115-120 |
| ISSN号 | 0042207X |
| DOI | 10.1016/j.vacuum.2016.10.034 |
| 英文摘要 | Carbon-iron composite films with different thicknesses (50, 100 and 150 nm) were deposited by DC magnetron sputtering method using a composite target (Fe: 4 at%, C: 96 at%). The resistive switching behaviors of Pt/Al/a-C:Fe/Au/Ti structures with different a-C:Fe film thicknesses are investigated. Abnormal bipolar resistive switching characteristics were observed in all Pt/Al/a-C:Fe/Au/Ti memory cells. Considering the endurance and retention properties, the RRAM cell with 100 nm thick a-C:Fe film as the dielectric layer showed the best performance with on/off-resistance ratio ∼10, and retention time >104s. Based on the results of the X-ray photoelectron spectroscopy depth profile, the resistive switching behavior is attributed to mutative Al3+fraction at the Al/a-C:Fe interface and the migration of Au ions between two electrodes. © 2016 Elsevier Ltd |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25664]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.School of Materials Science and Engineering, Shanghai University, Shanghai; 200444, China; 2.Solid State Physics and Materials, Suzhou University of Science and Technology, Suzhou; Jiangsu; 215011, China; 3.Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China |
| 推荐引用方式 GB/T 7714 | Zhou, J.W.,Li, T.R.,Zhang, D.,et al. Abnormal bipolar resistive switching behavior in carbon-iron composite films with different thicknesses[J]. Vacuum,2017,135:115-120. |
| APA | Zhou, J.W..,Li, T.R..,Zhang, D..,Ren, B..,Zhang, S.W..,...&Wang, L.J..(2017).Abnormal bipolar resistive switching behavior in carbon-iron composite films with different thicknesses.Vacuum,135,115-120. |
| MLA | Zhou, J.W.,et al."Abnormal bipolar resistive switching behavior in carbon-iron composite films with different thicknesses".Vacuum 135(2017):115-120. |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。