Effect of nickel doping on dielectric, piezoelectric properties and domain configurations of PZT based ceramics
文献类型:期刊论文
作者 | Jaitanong, Nittaya1; Zeng, Huarong2; Li, Guorong2; Yin, Qingrui2; Chaipanich, Arnon3 |
刊名 | Materials Science Forum
![]() |
出版日期 | 2017 |
卷号 | 883页码:27-31 |
ISSN号 | 02555476 |
DOI | 10.4028/www.scientific.net/MSF.883.27 |
英文摘要 | The aims of present study were investigated the effect of nickel doping on the dielectric and piezoelectric properties of P(BN)ZT solid solution. P(BN)ZT powder doped with nickel nanoparticle in the composition of (1-x) PBNZT–xNi when x = 0, 2, 4, 6, 8 and 10 percent by mole. P(BN)ZT doped with nickel powder were calcined at 900 ºC for 2 h and sintered at the temperature range of 1150 -1250ºC for 2 h with heating/cooling rate of 5 ºC/min. The dielectric constant (Εr) and the dielectric loss tangent (tanδ) of all ceramics were measured at room temperature using LCR meter. The piezoelectric properties (d33) were measured at room temperature using d33meter. The micro and nano-domain structure was clearly observed by piezo-response force microscopy (PFM). From the results, it can be seen that the dielectric and piezoelectric decreased with increasing Ni particle of all composition (0.0-0.1 mol%). Moreover, PFM images show that the micro (180°) and nano (90°) domain are orientated at the surface region in submicron-scale of P(BN)ZT ceramics with doped nickel nanoparticle. © 2017 Trans Tech Publications, Switzerland. |
源URL | [http://ir.sic.ac.cn/handle/331005/25660] ![]() |
专题 | 中国科学院上海硅酸盐研究所 |
作者单位 | 1.Faculty of Science, Maejo University, Chiang Mai; 50290, Thailand; 2.Key Laboratory of Inorganic Functional Materials and Integrated Devices, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai; 200050, China; 3.Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai; 50200, Thailand |
推荐引用方式 GB/T 7714 | Jaitanong, Nittaya,Zeng, Huarong,Li, Guorong,et al. Effect of nickel doping on dielectric, piezoelectric properties and domain configurations of PZT based ceramics[J]. Materials Science Forum,2017,883:27-31. |
APA | Jaitanong, Nittaya,Zeng, Huarong,Li, Guorong,Yin, Qingrui,&Chaipanich, Arnon.(2017).Effect of nickel doping on dielectric, piezoelectric properties and domain configurations of PZT based ceramics.Materials Science Forum,883,27-31. |
MLA | Jaitanong, Nittaya,et al."Effect of nickel doping on dielectric, piezoelectric properties and domain configurations of PZT based ceramics".Materials Science Forum 883(2017):27-31. |
入库方式: OAI收割
来源:上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。