Post-treatment of nanopowders-derived Nd:YAG transparent ceramics by hot isostatic pressing
文献类型：期刊论文
| 作者 | Li, Shanshan1,2; Ma, Peng1; Zhu, Xingwen2; Jiang, Nan1; Ivanov, Maxim3,4; Li, Chaoyu1; Xie, Tengfei1; Kou, Huamin1; Shi, Yun1; Chen, Haohong1 |
| 刊名 | Ceramics International
 |
| 出版日期 | 2017 |
| 卷号 | 43期号:13页码:10013-10019 |
| ISSN号 | 02728842 |
| DOI | 10.1016/j.ceramint.2017.05.015 |
| 英文摘要 | Neodymium doped yttrium aluminum garnet (Nd:YAG) transparent ceramics were fabricated from Nd:YAG nanopowders synthesized via a reverse precipitation method by vacuum sintering and successive hot isostatic pressing (HIP) post-treatment. The powders obtained by calcining the precursor at 1100 °C for 4 h and then ball milling for 2 h with 0.5 wt% TEOS as sintering aid were used to fabricate Nd:YAG ceramics. The green bodies were vacuum sintered at 1500–1800 °C for 10 h, followed by the HIP at 1600 °C for 3 h in 200 MPa Ar atmosphere. Influence of the calcination temperature on the phase, morphology and particle size evolution of the nanopowders, as well as the optical transparency and microstructure of the obtained Nd:YAG ceramics before and after the HIP post-treatment was investigated in detail. It was found that for the post-treated 1800 °C-vacuum-sintered Nd:YAG ceramic sample, the in-line transmittance increased from 48.0% up to 81.2% at the lasing wavelength of 1064 nm. © 2017 Elsevier Ltd and Techna Group S.r.l. |
| 源URL | [http://ir.sic.ac.cn/handle/331005/25594]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | 1.Key Laboratory of Transparent and Opto-Functional Advanced Inorganic Materials, Shanghai Institute of Ceramics, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai; 200050, China; 2.School of Material Sciences and Engineering, Shanghai University, 99 Shangda Road, Shanghai; 200436, China; 3.Institute of Electrophysics, Ural Branch of Russian Academy of Sciences, 106 Amundsen Street, Ekaterinburg; 620016, Russia; 4.Ural Federal University, 19 Mira Avenue, Ekaterinburg; 620002, Russia; 5.Department of Excited State Spectroscopy, Institute of Low Temperature and Structure Research Polish Academy of Sciences, Wroclaw; 50-422, Poland |
| 推荐引用方式 GB/T 7714 | Li, Shanshan,Ma, Peng,Zhu, Xingwen,et al. Post-treatment of nanopowders-derived Nd:YAG transparent ceramics by hot isostatic pressing[J]. Ceramics International,2017,43(13):10013-10019. |
| APA | Li, Shanshan.,Ma, Peng.,Zhu, Xingwen.,Jiang, Nan.,Ivanov, Maxim.,...&Li, Jiang.(2017).Post-treatment of nanopowders-derived Nd:YAG transparent ceramics by hot isostatic pressing.Ceramics International,43(13),10013-10019. |
| MLA | Li, Shanshan,et al."Post-treatment of nanopowders-derived Nd:YAG transparent ceramics by hot isostatic pressing".Ceramics International 43.13(2017):10013-10019. |