A multifunctional superamphiphobic cotton fabric was fabricated by coating silica nanoparticles on the cotton fabric surface and further modification by 1H,1H,2H,2H-perfluorooctyltrichlorosilane (FOTS). The fluctuant woven fabric and the fluffy spherical SiO₂ nanoparticles constructed a dual micro/nano- structures. The surface free energy of the fabric composite was reduced by FOTS modifier. The interplay of the structured and perfluorinated SiO₂ nanoparticles could not only endow the fabric highly liquid repellent ability, but could also to enhance the coating stability. The prepared cotton fabrics exhibited high liquid repellency to water, colza oil and n-hexadecane with lower surface tension, showing a con tact angle of 158°, 152°, and 153°, respectively. The results demonstrated that superamphiphobic cotton fabric possessed desirable chemical and mechanical durability, self-cleaning and self-healing property, the robust and multifunctional fabric would find innovative opportunities for practical applications.