Effects of stress-relief pre-annealing on deuterium trapping and diffusion in tungsten
文献类型：期刊论文
| 作者 | Zhu, Xiu-Li1,2; Cheng, Long1,2; De Temmerman, Gregory3; Shi, Li-Qun4; Yuan, Yue1,2; Wang, Bao-Yi5; Cao, Xing-Zhong5; Lu, Er-Yang5; Zhang, Ying1,2; Lu, Guang-Hong1,2 |
| 刊名 | Fusion engineering and design
 |
| 出版日期 | 2017-12-01 |
| 卷号 | 125页码:526-530 |
| 关键词 | Deuterium Tungsten Stress-relief pre-annealing Residual stresses |
| ISSN号 | 0920-3796 |
| DOI | 10.1016/j.fusengdes.2017.05.007 |
| 通讯作者 | Zhang, ying(zhyi@buaa.edu.cn) |
| 英文摘要 | Positron annihilation doppler broadening spectroscopy (pa-dbs) with slow positrons was utilized to characterize the change of vacancy-type defects induced by a stress-relief annealing (1273 k for 1 h in vacuum) as pre-annealing can remove not only residual stresses but also most intrinsic defects of the material. deuterium behavior after low energy (40 ev/d) and high-flux (10(24) d/m(2) s) plasma exposure was analyzed by a combination of pa-dbs, elastic recoil detection analysis (erda) and thermal desorption spectroscopy (tds). it is found that the vacancy defects density in tungsten is largely decreased by annealing and some intrinsic vacancies clusters to be multi-vacancies during the annealing process. with deuterium plasma exposure, a general decrease of s parameter found in both non-and pre-annealed tungsten suggests the deuterium occupation of vacancy-type defects. in combination of the s parameter change in the non-and pre-annealed tungsten, it is implied that deuterium trapping ability of vacancy type defects is constrained due to the residual stresses. this confinement effect concentrates on the top surface and it becomes weaker with increasing depth. a similar deuterium distribution in the near surface of non-and pre-annealed tungsten supports this confinement effect. in addition, comparing the amount of deuterium retained in the near surface and in the bulk suggests that the residual stress facilitate deuterium to diffuse into a larger depth in tungsten. (c) 2017 elsevier b.v. all rights reserved. |
| WOS关键词 | TEMPERATURE-DEPENDENCE ; POSITRON-ANNIHILATION ; LOW-ENERGY ; HIGH-FLUX ; RETENTION ; PLASMA ; DEFECTS ; BEAM ; ITER |
| WOS研究方向 | Nuclear Science & Technology |
| WOS类目 | Nuclear Science & Technology |
| 语种 | 英语 |
| WOS记录号 | WOS:000419407300081 |
| 出版者 | ELSEVIER SCIENCE SA |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2177895 |
| 专题 | 高能物理研究所 |
| 通讯作者 | Zhang, Ying |
| 作者单位 | 1.Beihang Univ, Dept Phys, Beijing 100191, Peoples R China 2.Beihang Univ, Beijing Key Lab Adv & Phys, Beijing 100191, Peoples R China 3.ITER Org, Route Vinon Verdon,CS90 046, F-13067 St Paul Les Durance, France 4.Fudan Univ, Inst Modern Phys, Shanghai 200433, Peoples R China 5.Chinese Acad Sci, Inst High Energy Phys, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhu, Xiu-Li,Cheng, Long,De Temmerman, Gregory,et al. Effects of stress-relief pre-annealing on deuterium trapping and diffusion in tungsten[J]. Fusion engineering and design,2017,125:526-530. |
| APA | Zhu, Xiu-Li.,Cheng, Long.,De Temmerman, Gregory.,Shi, Li-Qun.,Yuan, Yue.,...&Lu, Guang-Hong.(2017).Effects of stress-relief pre-annealing on deuterium trapping and diffusion in tungsten.Fusion engineering and design,125,526-530. |
| MLA | Zhu, Xiu-Li,et al."Effects of stress-relief pre-annealing on deuterium trapping and diffusion in tungsten".Fusion engineering and design 125(2017):526-530. |
入库方式： iSwitch采集
来源：高能物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。