Adjustment of biomass product gas to raise H-2/CO ratio and remove tar over sodium titanate catalysts
文献类型：期刊论文
| 作者 | Yuan, Hongyou1,2; Wu, Shubin1; Yin, Xiuli2; Huang, Yanqin2; Guo, Daliang2; Wu, Chuangzhi2 |
| 刊名 | RENEWABLE ENERGY
 |
| 出版日期 | 2018 |
| 卷号 | 115页码:288-298 |
| 关键词 | Biomass Pyrolysis Gasification Steam Reforming H-2/co Ratio Sodium Titanate |
| DOI | 10.1016/j.renene.2017.08.025 |
| 文献子类 | Article |
| 英文摘要 | To raise H-2/CO and remove tar for biomass product gas, sodium titanates 4Na(2)O center dot 5TiO(2) and Na2O center dot 3TiO(2) were evaluated at 850 degrees C using wood powder pyrolysis gas produced from a 0.3 kg/h screw pyrolyzer with no extra steam, silica sand was selected as an inert material for comparison. The GHSV of the runs were around 2000 h(-1) with tar content of about 200 g/Nm(3). The results suggest that 4Na(2)O center dot 5TiO(2) presents the highest activity, Na2O center dot 3TiO(2) ranks slightly lower, and silica sand shows no activity of enhancing hydrogen yield. The hydrogen formation is promoted through tar cracking, water gas shift and/or methane reforming. The H-2/CO increases to 1.8-2.0, which is higher than that of silica sand (about 0.35) and raw gas (about 0.25). Tar conversion in the 4Na(2)O center dot 5TiO(2) reforming was about 99% and nearly no coke was formed within the test duration of about 8 h, whereas the silica sand was coked obviously in 1 h. Most tar components can be effectively reformed, except for parts of xylene, naphthalene, biphenylene, and anthracene. The activity of 4Na(2)O center dot 5TiO(2) decreases gradually in the long-term test because of the release of sodium and has a tendency to transform to Na2O center dot 3TiO(2), the latter exhibits satisfactory stability and activity. (C) 2017 Elsevier Ltd. All rights reserved. |
| WOS关键词 | HYDROGEN-RICH GAS ; MOLTEN-CARBONATE SALTS ; STEAM GASIFICATION ; SYNGAS PRODUCTION ; NICKEL-CATALYSTS ; PRETREATED OLIVINE ; CO2 GASIFICATION ; MODEL-COMPOUND ; ALKALINE-EARTH ; SHIFT REACTION |
| 语种 | 英语 |
| WOS记录号 | WOS:000413615500027 |
| 资助机构 | National Natural Science Foundation of China(NSFC 51506206 ; National Key Basic Research Program of China(2013CB228101) ; Guangdong Provincial Science and Technology Plan Project(2016A010104011) ; 51661145022) |
| 源URL | [http://ir.giec.ac.cn/handle/344007/15858]  |
| 专题 | 中国科学院广州能源研究所 |
| 作者单位 | 1.South China Univ Technol, State Key Lab Pulp & Paper Engn, 51C0640, Guangzhou, Guangdong, Peoples R China 2.Chinese Acad Sci, Guangzhou Inst Energy Convers, Key Lab Renewable Energy, Guangzhou 510640, Guangdong, Peoples R China |
| 推荐引用方式 GB/T 7714 | Yuan, Hongyou,Wu, Shubin,Yin, Xiuli,et al. Adjustment of biomass product gas to raise H-2/CO ratio and remove tar over sodium titanate catalysts[J]. RENEWABLE ENERGY,2018,115:288-298. |
| APA | Yuan, Hongyou,Wu, Shubin,Yin, Xiuli,Huang, Yanqin,Guo, Daliang,&Wu, Chuangzhi.(2018).Adjustment of biomass product gas to raise H-2/CO ratio and remove tar over sodium titanate catalysts.RENEWABLE ENERGY,115,288-298. |
| MLA | Yuan, Hongyou,et al."Adjustment of biomass product gas to raise H-2/CO ratio and remove tar over sodium titanate catalysts".RENEWABLE ENERGY 115(2018):288-298. |
入库方式： OAI收割
来源：广州能源研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。