Organic nanocolumn arrays and organic solar cells
文献类型：会议论文
| 作者 | Zhang J(张坚) ; SALZMANNIngo ; SCHÄ ; FERPeter ; RABEJürgenP. ; KOCHNorbert |
| 出版日期 | 2009-09-13 |
| 会议名称 | 第十三届亚洲化学会 |
| 会议日期 | 2009-9-13 |
| 会议地点 | china |
| 页码 | 42/1 |
| 通讯作者 | 张坚 |
| 中文摘要 | in the past decade, the power conversion efficiency of organic solar cells had been prominently improvemed. these increases were achieved in both polymer and small-molecule organic solar cells through the use of the bulk heterojunction. ideally, the two phases of donor and acceptor materials should alternate on the length scale of the exciton diffusion length, and the two phases should be interdigitated and crystalline, to ensure high charge carrier mobility and reduced recombination. crystalline nanocolumn arrays of two widely studied organic semiconductors, i.e., fullerene (c60) and pentacene, were fabricated by glancing angle deposition (glad), and characterized by scanning electron microscopy and x-ray diffraction (fig. 1) [1,2]. for both materials, column diameters of typically 100 nm are found on the transparent conductive oxide ito, essentially independent of column height (up to 360 nm for pentacene). the molecular surface diffusion length on the substrate is identified as a critical parameter for the formation of columnar nanostructures by glad. then, organic solar cells were fabricated as small area sandwich devices. the pentacene nanocolumn array was deposited by glad on a pre-cleaned indium tin oxide (ito)/glass substrate. the pcbm was purchased from nanoc and used as received. the pcbm solution was spin-coated on top of the pentacene nanocolumn array. the devices were finalized by the deposition of a ~100 nm samarium through a shadow mask. device preparation was performed under ambient condictions, except for the evaporation of the top electrod. devices were characterized in a dry-argon atmosphere. current-voltage characteristics were measured using a keithley 2400 smu. devices clearly exhibited the rectifying behaviour in dark and photovoltaic effect under illumination. |
| 会议主办者 | chinese chemical society |
| 学科主题 | 物理化学 |
| 语种 | 中文 |
| 源URL | [http://159.226.238.44/handle/321008/113810]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 推荐引用方式 GB/T 7714 | Zhang J,SALZMANNIngo,SCHÄ,et al. Organic nanocolumn arrays and organic solar cells[C]. 见:第十三届亚洲化学会. china. 2009-9-13. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。