Self-assembly of polyelectrolyte multilayer pervaporation membranes by a dynamic layer-by-layer technique on a hydrolyzed polyacrylonitrile ultrafiltration membrane
文献类型：期刊论文
| 作者 | Liu, Zhongzhou; Yan, Haihong; Zhang, Guojun; Ji, Shulan |
| 刊名 | JOURNAL OF MEMBRANE SCIENCE
 |
| 出版日期 | 2007-04-05 |
| 卷号 | 292期号:1页码:1-8 |
| 关键词 | Polyelectrolyte Multilayer Membranes (Pemms) Dynamic Layer-by-layer Process Hydrolysis Polyacrylonitrile (Pan) Pervaporation Water/alcohol Mixture |
| 英文摘要 | This paper is concerned with the self-assembly of polyelectrolyte multilayer membranes (PEMMs) by using dynamic layer-by-layer (LBL) adsorption technique for pervaporation separation of water/alcohol mixtures. The polyacrylonitrile (PAN) ultrafiltration membrane used as a support was firstly hydrolyzed with alkaline solutions followed by alternatively depositing polyethylenei mine (PEI) and polyacrylic acid (PAA) under a pressure of 0.1 MPa. The PEI-ethanol solution and PEI-aqueous solution were used to investigate the effects of solvents on the assembly process. It was found that both separation factor and permeate flux were improved remarkably by replacing PEI aqueous solution with PEI-ethanol solution. Because only a few composite bilayers were needed to achieve a good capability in the dynamic LBL process, the hydrolysis degrees of PAN support membrane would strongly affect the pervaporation membrane performances. It was also noted that the exposure of membranes to low pH after hydrolysis would not benefit for the assembly. Further studies were conducted to investigate the effects of alkali species on the PAN hydrolysis and pervaporation performances of PEMMs. The contribution of alkali species on the pervaporation performance was in the order of KOH > NaOH > LiOH. Finally, the performances of PEI/PAA multilayer membranes assembled on the hydrolyzed PAN support were evaluated with a relatively wide range of feed temperature and concentration. The PEMMs obtained with only 2.5 bilayers had a separation factor of 604 and a permeate flux of 314 g/m(2)h (70 degrees C) for pervaporation of 95 wt% ethanol-water mixture. (c) 2007 Elsevier B.V. All rights reserved. |
| WOS记录号 | WOS:000245795300001 |
| 源URL | [http://ir.rcees.ac.cn/handle/311016/22615]  |
| 专题 | 生态环境研究中心_水污染控制实验室 |
| 推荐引用方式 GB/T 7714 | Liu, Zhongzhou,Yan, Haihong,Zhang, Guojun,et al. Self-assembly of polyelectrolyte multilayer pervaporation membranes by a dynamic layer-by-layer technique on a hydrolyzed polyacrylonitrile ultrafiltration membrane[J]. JOURNAL OF MEMBRANE SCIENCE,2007,292(1):1-8. |
| APA | Liu, Zhongzhou,Yan, Haihong,Zhang, Guojun,&Ji, Shulan.(2007).Self-assembly of polyelectrolyte multilayer pervaporation membranes by a dynamic layer-by-layer technique on a hydrolyzed polyacrylonitrile ultrafiltration membrane.JOURNAL OF MEMBRANE SCIENCE,292(1),1-8. |
| MLA | Liu, Zhongzhou,et al."Self-assembly of polyelectrolyte multilayer pervaporation membranes by a dynamic layer-by-layer technique on a hydrolyzed polyacrylonitrile ultrafiltration membrane".JOURNAL OF MEMBRANE SCIENCE 292.1(2007):1-8. |
入库方式： OAI收割
来源：生态环境研究中心
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。