Antifouling by pre-deposited Al hydrolytic flocs on ultrafiltration membrane in the presence of humic acid and bovine serum albumin
文献类型：期刊论文
| 作者 | Ma, Baiwen; Wang, Xing; Hu, Chengzhi; Jefferson, William A.; Liu, Huijuan; Qu, Jiuhui |
| 刊名 | JOURNAL OF MEMBRANE SCIENCE
 |
| 出版日期 | 2017-09-15 |
| 卷号 | 538期号:0页码:34-40 |
| 关键词 | Ultrafiltration Membrane Humic Acid And Bovine Serum Albumin Al-based Flocs Pre-deposition Fouling Alleviation |
| 英文摘要 | Pre-deposition technology is a promising method for alleviating membrane fouling, and in situ hydrolytic flocs have strong adsorption ability. In comparison with iron salts, less corrosiveness is induced by aluminum salts. Here, flocs formed by aluminum salts were pre-deposited onto the surface of an ultrafiltration (UF) membrane, aimed at investigating the antifouling performance with humic acid (HA) or bovine serum albumin (BSA). The results showed that Al-based flocs were well distributed onto the membrane surface, and a relatively dense and homogeneous deposition layer was formed. Both HA and BSA could largely be adsorbed/rejected by the pre-deposited layer during filtration. In comparison to results for solution pH of 8.0, the floc layer was much denser with a larger surface specific area and smaller average pore diameter at pH 6.0. Due to the existence of Al-13 species, a more positively charged floc layer occurred at lower pH values, leading to stronger adsorption abilities toward the negatively charged HA and BSA molecules. The floc layer significantly reduced the possibility of HA and BSA molecules reaching the UF membrane, which helped alleviate membrane fouling under lower pH conditions. Furthermore, the results for effluent with pH between 6.0 and 8.0 showed that the removal efficiency of HA molecules with small molecular weight (< 3 kDa) was also higher, especially at pH 6.0. |
| 源URL | [http://ir.rcees.ac.cn/handle/311016/39666]  |
| 专题 | 生态环境研究中心_中国科学院饮用水科学与技术重点实验室 |
| 推荐引用方式 GB/T 7714 | Ma, Baiwen,Wang, Xing,Hu, Chengzhi,et al. Antifouling by pre-deposited Al hydrolytic flocs on ultrafiltration membrane in the presence of humic acid and bovine serum albumin[J]. JOURNAL OF MEMBRANE SCIENCE,2017,538(0):34-40. |
| APA | Ma, Baiwen,Wang, Xing,Hu, Chengzhi,Jefferson, William A.,Liu, Huijuan,&Qu, Jiuhui.(2017).Antifouling by pre-deposited Al hydrolytic flocs on ultrafiltration membrane in the presence of humic acid and bovine serum albumin.JOURNAL OF MEMBRANE SCIENCE,538(0),34-40. |
| MLA | Ma, Baiwen,et al."Antifouling by pre-deposited Al hydrolytic flocs on ultrafiltration membrane in the presence of humic acid and bovine serum albumin".JOURNAL OF MEMBRANE SCIENCE 538.0(2017):34-40. |
入库方式： OAI收割
来源：生态环境研究中心
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。