Study on the High Temperature Interfacial Stability of Ti/Mo/Yb0.3Co4Sb12 Thermoelectric Joints
文献类型：期刊论文
| 作者 | Gu, Ming; Bai, Shengqiang; Xia, Xugui; Huang, Xiangyang; Li, Xiaoya; Shi, Xun; Chen, Lidong |
| 刊名 | APPLIED SCIENCES-BASEL
 |
| 出版日期 | 2017 |
| 卷号 | 7期号:9 |
| ISSN号 | 2076-3417 |
| DOI | 10.3390/app7090952 |
| 英文摘要 | To improve the interfacial stability at high temperatures, n-type skutterudite (SKD) thermoelectric joints with sandwich structures of Ti/Mo/Yb0.3Co4Sb12 were successfully designed and fabricated. In this structure, Mo and Ti were introduced as the barrier layer with the goal of suppressing the interfacial diffusion and the buffer layer with the goal of enhancing the bonding strength, respectively. To evaluate the high temperature interfacial behavior of the Ti/Mo/Yb0.3Co4Sb12 joints, thermal shocking between 0 degrees C and 600 degrees C and isothermal aging at a temperature range of 550 degrees C to 650 degrees C were carried out in vacuum. During the isothermal aging process, Ti penetrates across the Mo layer, and finally diffuses into the Yb0.3Co4Sb12 matrix. By increasing the isothermal aging time, Ti continuously diffuses and reacts with the elements of Sb and Co in the matrix, consequently forming the multilayer-structured intermetallic compounds of Ti3Sb/Ti2Sb/TiCoSb. Diffusion kinetics was investigated and it was found that the interfacial evolution of the Ti/Mo/Yb0.3Co4Sb12 joints was a diffusion-controlling process. During the diffusion process, the formed Mo-Ti buffer layer acts as a damper, which greatly decelerates the diffusion of Ti towards the Yb0.3Co4Sb12 matrix at high temperatures. Meanwhile, it was found that the increase in the contact resistivity of the joints mainly derives from the inter-diffusion between Ti and Yb0.3Co4Sb12. As a result, the Ti/Mo/Yb0.3Co4Sb12 joint demonstrates the excellent stability of the interfacial contact resistivity. Service life prediction was made based on the stability of the contact resistivity, and it was found that the Ti/Mo/Yb0.3Co4Sb12 joint is qualified for practical applications at 550 degrees C. |
| WOS记录号 | WOS:000414453600088 |
| 源URL | [http://ir.sic.ac.cn/handle/331005/26647]  |
| 专题 | 中国科学院上海硅酸盐研究所 |
| 作者单位 | Chinese Acad Sci, State Key Lab High Performance Ceram & Superfine, Shanghai Inst Ceram, 1295 Dingxi Rd, Shanghai 200050, Peoples R China |
| 推荐引用方式 GB/T 7714 | Gu, Ming,Bai, Shengqiang,Xia, Xugui,et al. Study on the High Temperature Interfacial Stability of Ti/Mo/Yb0.3Co4Sb12 Thermoelectric Joints[J]. APPLIED SCIENCES-BASEL,2017,7(9). |
| APA | Gu, Ming.,Bai, Shengqiang.,Xia, Xugui.,Huang, Xiangyang.,Li, Xiaoya.,...&Chen, Lidong.(2017).Study on the High Temperature Interfacial Stability of Ti/Mo/Yb0.3Co4Sb12 Thermoelectric Joints.APPLIED SCIENCES-BASEL,7(9). |
| MLA | Gu, Ming,et al."Study on the High Temperature Interfacial Stability of Ti/Mo/Yb0.3Co4Sb12 Thermoelectric Joints".APPLIED SCIENCES-BASEL 7.9(2017). |
入库方式： OAI收割
来源：上海硅酸盐研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。