Preparation and solidification process of mono-sized Cu–Ni–Sn microspheres by pulsated orifice ejection method
文献类型：期刊论文
| 作者 | Li,Can1,2; Li,Jianqiang2; Hu,Yingyan2; Liu,Chao1; Li,Xiaoyu2 |
| 刊名 | Materials Research Express
 |
| 出版日期 | 2019-02-06 |
| 卷号 | 6期号:5 |
| 关键词 | mono-sized Cu–Ni–Sn microspheres sphericity pulsated orifice ejection method rapid solidification secondary dendrite arm spacing |
| ISSN号 | 2053-1591 |
| DOI | 10.1088/2053-1591/ab0187 |
| 英文摘要 | Abstract Cu–Ni–Sn alloys are well known for their excellent properties, including excellent elasticity and high strength, which enable large potentials for applications in microelectronic industry and 3D printing for example. Preparation of the high quality spherical powders should meet the new requirements in these emerging fields. In this work, the mono-sized Cu-13Ni-17Sn (wt%) microspheres with controllable diameters ranging from 84.4 μm to 212.0 μm were prepared by pulsated orifice ejection method (POEM). Solidified Cu–Ni–Sn microspheres exhibit good sphericity and remarkably narrowed size distribution. The percentage of microspheres with sphericity of more than 0.9 is high up to 98.6%, and the average sphericity of microspheres is 0.989. The surface of Cu–Ni–Sn microspheres is smooth, and the interior contains no pores and impurities. Furthermore, the cooling rate of Cu-13Ni-17Sn microspheres was estimated in a Newton’s cooling model. With decreasing particle diameter, the cooling rate of Cu-13Ni-17Sn microspheres increases gradually. When the particle diameter is less than 84.4 μm, the cooling rate of microspheres exceeds 3.64?×?104 K s?1. With increasing particle size, the secondary dendrite arm spacing increases gradually owing to the decrease of the sphere cooling rate. |
| 语种 | 英语 |
| WOS记录号 | IOP:2053-1591-6-5-AB0187 |
| 出版者 | IOP Publishing |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/27527]  |
| 专题 | 中国科学院过程工程研究所 |
| 作者单位 | 1.State Key Laboratory of Silicate Materials for Architectures, Wuhan University of Technology, 122 Luoshi Road, Hongshan, Wuhan, Hubei 430070, People’s Republic of China 2.National Engineering Laboratory for Hydrometallurgical Cleaner Production Technology, CAS Key Laboratory of Green Process and Engineering, Institute of Process Engineering, Chinese Academy of Sciences, Beijing 100190, People’s Republic of China |
| 推荐引用方式 GB/T 7714 | Li,Can,Li,Jianqiang,Hu,Yingyan,et al. Preparation and solidification process of mono-sized Cu–Ni–Sn microspheres by pulsated orifice ejection method[J]. Materials Research Express,2019,6(5). |
| APA | Li,Can,Li,Jianqiang,Hu,Yingyan,Liu,Chao,&Li,Xiaoyu.(2019).Preparation and solidification process of mono-sized Cu–Ni–Sn microspheres by pulsated orifice ejection method.Materials Research Express,6(5). |
| MLA | Li,Can,et al."Preparation and solidification process of mono-sized Cu–Ni–Sn microspheres by pulsated orifice ejection method".Materials Research Express 6.5(2019). |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。