Degradation study on MEA in H3PO4/PBI high-temperature PEMFC life test
文献类型：期刊论文
| 作者 | Zhai, Yunfeng; Zhang, Huamin; Liu, Gang; Hu, Jingwei; Yia, Baolian |
| 刊名 | journal of the electrochemical society
 |
| 出版日期 | 2007 |
| 卷号 | 154期号:1页码:b72-b76 |
| 产权排序 | 1;1 |
| 通讯作者 | 张华民 |
| 英文摘要 | in this paper, 550 h (500 h continuous and 50 h intermittent) high-temperature proton exchange membrane fuel cell (pemfc, phosphoric acid-doped polybenzimidazole system, h3po4/pbi) life test was performed without humidification at 150 degrees c; constant current (at 640 ma cm(-2)) performance and polarization curves were recorded. electrochemical and physical characterizations were applied to investigate the degradation of the membrane electrode assembly (mea). the results showed that the constant current performance started to reduce with a rate of 0.18 mv h(-1) after about 90 h activation. surface area loss of the cathode platinum due to agglomeration was detected by cyclic voltammetry and transmission electron microscopy. a slight increase of internal resistance of the single cell due to h3po4 leaching was found by electrochemical impedance spectroscopy and energy dispersive x-ray analysis. h-2 permeability of mea increased during the last 50 h intermittent test because of appearing of cracks, that were detected by linear sweep voltammetry and scanning electron microscopy. these results suggested that catalyst agglomeration and h3po4 leaching from catalyst layers contributed to the performance degradation of the mea during the life test, and mechanical properties degradation of h3po4/pbi membrane impacted badly the lifetime of the single cell. (c) 2006 the electrochemical society. |
| WOS标题词 | science & technology ; physical sciences ; technology |
| 类目[WOS] | electrochemistry ; materials science, coatings & films |
| 研究领域[WOS] | electrochemistry ; materials science |
| 关键词[WOS] | acid doped polybenzimidazole ; membrane fuel-cells ; polymer electrolyte ; phosphoric-acid ; supported platinum ; oxygen reduction ; carbon ; conductivity ; operation |
| 收录类别 | SCI |
| 原文出处 | true |
| 语种 | 英语 |
| WOS记录号 | WOS:000242538600022 |
| 公开日期 | 2010-11-30 |
| 源URL | [http://159.226.238.44/handle/321008/99505]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | 1.Chinese Acad Sci, Dalian Inst Chem Phys, Proton Exchange Membrane Fuel Cell Key Mat & Tech, Dalian 116023, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhai, Yunfeng,Zhang, Huamin,Liu, Gang,et al. Degradation study on MEA in H3PO4/PBI high-temperature PEMFC life test[J]. journal of the electrochemical society,2007,154(1):b72-b76. |
| APA | Zhai, Yunfeng,Zhang, Huamin,Liu, Gang,Hu, Jingwei,&Yia, Baolian.(2007).Degradation study on MEA in H3PO4/PBI high-temperature PEMFC life test.journal of the electrochemical society,154(1),b72-b76. |
| MLA | Zhai, Yunfeng,et al."Degradation study on MEA in H3PO4/PBI high-temperature PEMFC life test".journal of the electrochemical society 154.1(2007):b72-b76. |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。