Long-term Behavior of Fiber Reinforced Concrete Exposed to Sulfate Solution Cycling in Drying-immersion
文献类型：期刊论文
| 作者 | Geng Yongjuan1; Jin Zuquan1; Hou Baorong2; Zhao Tiejun1; Gao Song1 |
| 刊名 | JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION
 |
| 出版日期 | 2017-08-01 |
| 卷号 | 32期号:4页码:875-881 |
| 关键词 | Fiber Reinforced Concrete Sulfate Ion Damage Diffusion Coefficient Drying-immersion Cycles |
| DOI | 10.1007/s11595-017-1683-x |
| 文献子类 | Article |
| 英文摘要 | The damage process and corrosion ion distribution in concrete, which was exposed to 60 and 170 drying-immersion cycles of sulfate solution, were systematically investigated. The effects of plain concrete, plain concrete mixed with 4 and 8 kg/m(3) modified PP fiber and high-performance concrete (HPC) mixed with 0.8 kg/m(3) fine PP fiber on the damage process were also studied. The experimental results showed that thenardite-induced surface scaling, as well as gypsum-and ettringite-induced cracks, were the main degradation forms of concrete under attack of sulfate solution and drying-immersion cycles. The relative dynamic modulus of elasticity of concrete initially increased, then reached stability and finally decreased to failure. The sulfate diffusion coefficients of plain and HPC were 10(-12) and 10(-13) m(2)/s, respectively. The concentration of sodium ion increased with depth, then maintained stability and finally decreased rapidly with concrete depth. The content of calcium ion on the concrete surface was 110%-150% of that in the interior of specimens. Although fiber worsened the surface scaling of concrete, better resistance capacity of sulfate ion penetration into concrete was observed in plain concrete with 4 kg/m(3) modified PP fiber and HPC. |
| 语种 | 英语 |
| WOS记录号 | WOS:000407684600022 |
| 版本 | 出版稿 |
| 源URL | [http://ir.qdio.ac.cn/handle/337002/143091]  |
| 专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
| 作者单位 | 1.Qingdao Technol Univ, Sch Civil Engn, Qingdao 266033, Peoples R China 2.Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China |
| 推荐引用方式 GB/T 7714 | Geng Yongjuan,Jin Zuquan,Hou Baorong,et al. Long-term Behavior of Fiber Reinforced Concrete Exposed to Sulfate Solution Cycling in Drying-immersion[J]. JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION,2017,32(4):875-881. |
| APA | Geng Yongjuan,Jin Zuquan,Hou Baorong,Zhao Tiejun,&Gao Song.(2017).Long-term Behavior of Fiber Reinforced Concrete Exposed to Sulfate Solution Cycling in Drying-immersion.JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION,32(4),875-881. |
| MLA | Geng Yongjuan,et al."Long-term Behavior of Fiber Reinforced Concrete Exposed to Sulfate Solution Cycling in Drying-immersion".JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION 32.4(2017):875-881. |
入库方式： OAI收割
来源：海洋研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。