Effects of sulfate-reducing bacteria on the corrosion behavior of carbon steel
文献类型：期刊论文
| 作者 | Kuang, Fei; Wang, Jia ; Yan, Li; Zhang, Dun
|
| 刊名 | ELECTROCHIMICA ACTA
 |
| 出版日期 | 2007-06-10 |
| 卷号 | 52期号:20页码:6084-6088 |
| 关键词 | Sulfate-reducing Bacteria Microbiologically Induced Corrosion Medium State D36 Carbon Steel Corrosion Rate |
| ISSN号 | 0013-4686 |
| DOI | 10.1016/j.electacta.2007.03.041 |
| 文献子类 | Article |
| 英文摘要 | The influences of the growing process of sulfate-reducing bacteria (SRB) in seawater system on the medium state and corrosion behavior of carbon steel were studied by detecting solution state parameters and using corrosion electrochemical methods. The growing process of SRB in the seawater shows the three stages of growing, death and residual phases. The solution state parameters of the concentration of sulfide, the pH value and the redox potential changed during the three stages of the SRB growing process. And the corrosion rate of D36 carbon steel was accelerated during the growing phase and stable during the death and residual phases. The results indicate that the medium state and the corrosion rate of the steel do not depend on the number of active SRB, but depend on the accumulation of the metabolism products of SRB. (c) 2007 Elsevier Ltd. All rights reserved.; The influences of the growing process of sulfate-reducing bacteria (SRB) in seawater system on the medium state and corrosion behavior of carbon steel were studied by detecting solution state parameters and using corrosion electrochemical methods. The growing process of SRB in the seawater shows the three stages of growing, death and residual phases. The solution state parameters of the concentration of sulfide, the pH value and the redox potential changed during the three stages of the SRB growing process. And the corrosion rate of D36 carbon steel was accelerated during the growing phase and stable during the death and residual phases. The results indicate that the medium state and the corrosion rate of the steel do not depend on the number of active SRB, but depend on the accumulation of the metabolism products of SRB. (c) 2007 Elsevier Ltd. All rights reserved. |
| 学科主题 | Electrochemistry |
| URL标识 | 查看原文 |
| 语种 | 英语 |
| WOS记录号 | WOS:000247290900002 |
| 公开日期 | 2010-12-24 |
| 源URL | [http://ir.qdio.ac.cn/handle/337002/5165]  |
| 专题 | 海洋研究所_海洋腐蚀与防护研究发展中心 |
| 作者单位 | 1.Ocean Univ China, Qingdao 266100, Peoples R China 2.Chinese Acad Sci, Inst Oceanol, Qingdao 266071, Peoples R China 3.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China 4.Ocean Univ China, Qingdao 266100, Peoples R China 5.State Key Lab Corros & Protect, Shenyang 110015, Peoples R China |
| 推荐引用方式 GB/T 7714 | Kuang, Fei,Wang, Jia,Yan, Li,et al. Effects of sulfate-reducing bacteria on the corrosion behavior of carbon steel[J]. ELECTROCHIMICA ACTA,2007,52(20):6084-6088. |
| APA | Kuang, Fei,Wang, Jia,Yan, Li,&Zhang, Dun.(2007).Effects of sulfate-reducing bacteria on the corrosion behavior of carbon steel.ELECTROCHIMICA ACTA,52(20),6084-6088. |
| MLA | Kuang, Fei,et al."Effects of sulfate-reducing bacteria on the corrosion behavior of carbon steel".ELECTROCHIMICA ACTA 52.20(2007):6084-6088. |
入库方式： OAI收割
来源：海洋研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。