Preparation and characterization of high boiling solvent lignin-based polyurethane film with lignin as the only hydroxyl group provider
文献类型：期刊论文
| 作者 | Jia, Zhen1,2; Lu, Chunxiang1; Zhou, Pucha1; Wang, Lu1,2 |
| 刊名 | Rsc advances
 |
| 出版日期 | 2015 |
| 卷号 | 5期号:66页码:53949-53955 |
| ISSN号 | 2046-2069 |
| DOI | 10.1039/c5ra09477a |
| 通讯作者 | Lu, chunxiang(chunxl@sxicc.ac.cn) |
| 英文摘要 | A novel diisocyanate-modified lignin-based polyurethane (lpu) film was facilely prepared using renewable lignin as the only hydroxyl group provider at ambient temperature and pressure for the first time. the lignin was extracted through a modified high boiling solvent (hbs) method with 1,4-dioxane as the solvent, and then dried through freeze drying. the ash content of the hbs lignin sample was about 0.25%, which was lower than for other lignins. the hbs lignin had a large number of hydroxyl groups, which indicated the potential value in substitution of polyols in the synthesis of polyurethane (pu). from the results, the lpu film possessed high performance in hardness, solvent resistance and hydrophilicity with no need for further modification. the lpu film also had high tensile strength with a maximum value of 41.6 mpa. in order to investigate the thermal properties of the lpu film, thermal gravimetric analysis (tga) and thermogravimetric infrared analysis (tga-ftir) were performed, and the lpu film was stable at 114 degrees c in air and an n-2 atmosphere. this study developed a novel lpu film which could show promising future applications as a coating and base. |
| WOS关键词 | BETA-GUAIACYL ETHER ; DELIGNIFICATION MECHANISM ; THERMAL-PROPERTIES ; ALCELL(R) LIGNIN ; TG-FTIR ; SPECTROSCOPY ; DEGRADATION ; COMPOSITES ; POLYOLS ; FOAMS |
| WOS研究方向 | Chemistry |
| WOS类目 | Chemistry, Multidisciplinary |
| 语种 | 英语 |
| WOS记录号 | WOS:000356801300096 |
| 出版者 | ROYAL SOC CHEMISTRY |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2376422 |
| 专题 | 中国科学院大学 |
| 通讯作者 | Lu, Chunxiang |
| 作者单位 | 1.Chinese Acad Sci, Inst Coal Chem, Natl Engn Lab Carbon Fiber Technol, Taiyuan 030001, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Jia, Zhen,Lu, Chunxiang,Zhou, Pucha,et al. Preparation and characterization of high boiling solvent lignin-based polyurethane film with lignin as the only hydroxyl group provider[J]. Rsc advances,2015,5(66):53949-53955. |
| APA | Jia, Zhen,Lu, Chunxiang,Zhou, Pucha,&Wang, Lu.(2015).Preparation and characterization of high boiling solvent lignin-based polyurethane film with lignin as the only hydroxyl group provider.Rsc advances,5(66),53949-53955. |
| MLA | Jia, Zhen,et al."Preparation and characterization of high boiling solvent lignin-based polyurethane film with lignin as the only hydroxyl group provider".Rsc advances 5.66(2015):53949-53955. |
入库方式： iSwitch采集
来源：中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。