Effect of poly(para-dioxanone) on the hydrolytic degradation of poly(l-lactide)
文献类型:期刊论文
作者 | Xie, Xulong1,2; Bai, Wei1,3; Chen, Dongliang1,3; Xiong, Chengdong1,3; Pang, Xiubing3 |
刊名 | Journal of polymers and the environment |
出版日期 | 2015-06-01 |
卷号 | 23期号:2页码:156-164 |
ISSN号 | 1566-2543 |
关键词 | Poly(l-lactide) Poly(para-dioxanone) Blends Hydrolytic degradation |
DOI | 10.1007/s10924-014-0670-y |
通讯作者 | Bai, wei(baiwei@cioc.ac.cn) |
英文摘要 | Poly(l-lactide) (plla) was blended with various contents of poly(para-dioxanone) (ppdo; 5, 10, 15 and 20 wt%) by solution co-precipitation to modify the degradation characteristics of plla. as ppdo degrades rapidly, it can be advantageously used in blends with plla. the in vitro hydrolytic degradation of the plla/ppdo blends was studied by weight loss (wl) analysis, water absorption (wa), the thermal properties, the surface morphology and the mechanical properties of the samples in phosphate-buffered saline (ph 7.44) at 37 degrees c over 8 weeks. during the degradation process, the wl and wa increased significantly for all blends and a fenestral structure with defects was formed on the surface of blend bars as degradation progressed. meanwhile, the glass transition temperature (t-g), melting temperature (t-m), tensile strength and breaking elongation of the blends decreased with time, whereas the hydrolysis rate of the blends varied with the blend composition. compared with plla, plla/ppdo blends exhibited a higher hydrolysis rate. |
WOS关键词 | PHASE MORPHOLOGY ANALYSIS ; MECHANICAL-PROPERTIES ; MOLECULAR-WEIGHTS ; BLENDS ; CRYSTALLIZATION ; NANOCOMPOSITES ; BIODEGRADATION ; BEHAVIOR ; POLY(EPSILON-CAPROLACTONE) ; POLY(P-DIOXANONE) |
WOS研究方向 | Engineering ; Polymer Science |
WOS类目 | Engineering, Environmental ; Polymer Science |
语种 | 英语 |
出版者 | SPRINGER/PLENUM PUBLISHERS |
WOS记录号 | WOS:000355234000002 |
URI标识 | http://www.irgrid.ac.cn/handle/1471x/2376592 |
专题 | 中国科学院大学 |
通讯作者 | Bai, Wei |
作者单位 | 1.Chinese Acad Sci, Chengdu Inst Organ Chem, Chengdu 610041, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100039, Peoples R China 3.Zhejiang Engn Res Ctr Biodegradable Med Mat, Dongyang 322100, Peoples R China |
推荐引用方式 GB/T 7714 | Xie, Xulong,Bai, Wei,Chen, Dongliang,et al. Effect of poly(para-dioxanone) on the hydrolytic degradation of poly(l-lactide)[J]. Journal of polymers and the environment,2015,23(2):156-164. |
APA | Xie, Xulong,Bai, Wei,Chen, Dongliang,Xiong, Chengdong,&Pang, Xiubing.(2015).Effect of poly(para-dioxanone) on the hydrolytic degradation of poly(l-lactide).Journal of polymers and the environment,23(2),156-164. |
MLA | Xie, Xulong,et al."Effect of poly(para-dioxanone) on the hydrolytic degradation of poly(l-lactide)".Journal of polymers and the environment 23.2(2015):156-164. |
入库方式: iSwitch采集
来源:中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。