Tribochemical effects on the friction and wear behaviors of diamond-like carbon film under high relative humidity condition
文献类型：期刊论文
| 作者 | Li, H; Xu, T; Wang, C; Chen, J; Zhou, H; Liu, H |
| 刊名 | Tribology letters
 |
| 出版日期 | 2005-07-01 |
| 卷号 | 19期号:3页码:231-238 |
| ISSN号 | 1023-8883 |
| 关键词 | Dlc film Friction Wear Tribochemical interaction |
| DOI | 10.1007/s11249-005-6150-8 |
| 通讯作者 | Li, h(xuanholi77@yahoo.com.cn) |
| 英文摘要 | Friction and wear behaviors of diamond-like carbon (dlc) film in humid n-2 (rh-100%) sliding against different counterpart ball (si3n4 ball, al2o3 ball and steel ball) were investigated. it was found that the friction and wear behaviors of dlc film were dependent on the friction-induced tribochemical interactions in the presence of the dlc film, water molecules and counterpart balls. when sliding against si3n4 ball, a tribochemical film that mainly consisted of silica gel was formed on the worn surface due to the oxidation and hydrolysis of the si3n4 ball, and resulted in the lowest friction coefficient and wear rate of the dlc film. the degradation of the dlc film catalyzed by al2o3 ball caused the highest wear rate of dlc film when sliding against al2o3 ball, while the tribochemical reactions between dlc film and steel ball led to the highest friction coefficient when sliding against steel ball. |
| WOS关键词 | RF PLASMA SYSTEM ; TRIBOLOGICAL BEHAVIOR ; DEGRADATION ; XPS ; ENVIRONMENTS ; POLYMERS ; OXYGEN ; STEEL ; WATER |
| WOS研究方向 | Engineering |
| WOS类目 | Engineering, Chemical ; Engineering, Mechanical |
| 语种 | 英语 |
| 出版者 | SPRINGER/PLENUM PUBLISHERS |
| WOS记录号 | WOS:000230717300009 |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2377463 |
| 专题 | 中国科学院大学 |
| 通讯作者 | Li, H |
| 作者单位 | 1.Chinese Acad Sci, Lanzhou Inst Chem Phys, State Key Lab Solid Lubricat, Lanzhou 730000, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li, H,Xu, T,Wang, C,et al. Tribochemical effects on the friction and wear behaviors of diamond-like carbon film under high relative humidity condition[J]. Tribology letters,2005,19(3):231-238. |
| APA | Li, H,Xu, T,Wang, C,Chen, J,Zhou, H,&Liu, H.(2005).Tribochemical effects on the friction and wear behaviors of diamond-like carbon film under high relative humidity condition.Tribology letters,19(3),231-238. |
| MLA | Li, H,et al."Tribochemical effects on the friction and wear behaviors of diamond-like carbon film under high relative humidity condition".Tribology letters 19.3(2005):231-238. |
入库方式： iSwitch采集
来源：中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。