Preparation of si3n4/sio2 composites with pressureless sintering
文献类型：期刊论文
| 作者 | Xu Chang-Ming; Wang Shi-Wei; Huang Xiao-Xian; Guo Jing-Kun |
| 刊名 | Journal of inorganic materials
 |
| 出版日期 | 2006-07-01 |
| 卷号 | 21期号:4页码:935-938 |
| 关键词 | Radome Pressureless sintering Si3n4/sio2 composites Mechanical properties Dielectric properties |
| ISSN号 | 1000-324X |
| 通讯作者 | Xu chang-ming() |
| 英文摘要 | Si3n4/sio2 composites were prepared with pressureless sintering. it was found that the si3n4 particle was effective to suppress the crystallization of cristobalite in the si3n4/sio2 composites and contributed to the improvement of the mechanical properties. after sintered at 1370 degrees c for 2h, the flexural strength of the composites with 5vol% si3n4 addition reached 96.2mpa, the fracture toughness was 2.4mpa.m(1/2). the dielectric constant and loss tangent of the composites was 3.63 similar to 3.68 and 1.29 similar to 1.75x 10(-3), respectively. |
| WOS研究方向 | Materials Science |
| WOS类目 | Materials Science, Ceramics |
| 语种 | 英语 |
| WOS记录号 | WOS:000240210700028 |
| 出版者 | SCIENCE CHINA PRESS |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2378451 |
| 专题 | 中国科学院大学 |
| 通讯作者 | Xu Chang-Ming |
| 作者单位 | 1.Chinese Acad Sci, Shanghai Inst Ceram, Shanghai 200050, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Xu Chang-Ming,Wang Shi-Wei,Huang Xiao-Xian,et al. Preparation of si3n4/sio2 composites with pressureless sintering[J]. Journal of inorganic materials,2006,21(4):935-938. |
| APA | Xu Chang-Ming,Wang Shi-Wei,Huang Xiao-Xian,&Guo Jing-Kun.(2006).Preparation of si3n4/sio2 composites with pressureless sintering.Journal of inorganic materials,21(4),935-938. |
| MLA | Xu Chang-Ming,et al."Preparation of si3n4/sio2 composites with pressureless sintering".Journal of inorganic materials 21.4(2006):935-938. |
入库方式： iSwitch采集
来源：中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。