Flux growth and optical properties of na3la9o3(bo3)(8) crystals
文献类型：期刊论文
| 作者 | Li, Yunge; Wu, Yicheng; Zhang, Guochun; Fu, Peizhen; Bai, Xiaoyan |
| 刊名 | Journal of crystal growth
 |
| 出版日期 | 2006-07-01 |
| 卷号 | 292期号:2页码:468-471 |
| 关键词 | Top-seeded solution growth Na3la9o3(bo3)(8) (nlbo) Second harmonic generation (shg) |
| ISSN号 | 0022-0248 |
| DOI | 10.1016/j.jcrysgro.2006.04.105 |
| 通讯作者 | Wu, yicheng(ycwu@cl.cryo.ac.cn) |
| 英文摘要 | Na3la9o3(bo3)(8) (nlbo) crystals were grown by the top-seeded solution growth (tssg) method from three new fluxes: na2o-b2o3-li2o, na2o-b2o3-naf-lif and na2o-b2o3-naf, respectively. the volatility was investigated. the results showed that the na2o-b2o3-naf flux is more suitable than others for growing nlbo crystals. the suitable molar ratio for na3la9o3(bo3)(8), na2co3, h3bo3 and naf is 1.0:(7.5 similar to 5.0):(6.5 similar to 5.0):(8.8 similar to 35.0) with the growth temperature at 920 similar to 980 degrees c. nlbo crystal size was up to 35 x 22 x 10 mm(3). the shortest shg wavelengths for type-i and type-ii phase-matching (pm) are 288 nm and 395 nm, respectively. (c) 2006 published by elsevier b.v. |
| WOS研究方向 | Crystallography ; Materials Science ; Physics |
| WOS类目 | Crystallography ; Materials Science, Multidisciplinary ; Physics, Applied |
| 语种 | 英语 |
| WOS记录号 | WOS:000239481000066 |
| 出版者 | ELSEVIER SCIENCE BV |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2378740 |
| 专题 | 中国科学院大学 |
| 通讯作者 | Wu, Yicheng |
| 作者单位 | 1.Chinese Acad Sci, Tech Inst Phys & Chem, Beijing 100080, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li, Yunge,Wu, Yicheng,Zhang, Guochun,et al. Flux growth and optical properties of na3la9o3(bo3)(8) crystals[J]. Journal of crystal growth,2006,292(2):468-471. |
| APA | Li, Yunge,Wu, Yicheng,Zhang, Guochun,Fu, Peizhen,&Bai, Xiaoyan.(2006).Flux growth and optical properties of na3la9o3(bo3)(8) crystals.Journal of crystal growth,292(2),468-471. |
| MLA | Li, Yunge,et al."Flux growth and optical properties of na3la9o3(bo3)(8) crystals".Journal of crystal growth 292.2(2006):468-471. |
入库方式： iSwitch采集
来源：中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。