Growth of zno single crystals by an induced nucleation from a high temperature solution of the zno-pbf2 system
文献类型：期刊论文
| 作者 | Li, Xinhua; Xu, Jiayue; Jin, Min; Wu, Xianjun; Qian, Guoxing; Li, Xiaomin |
| 刊名 | Crystal research and technology
 |
| 出版日期 | 2007-03-01 |
| 卷号 | 42期号:3页码:221-226 |
| 关键词 | Flux Single-crystal growth Zinc oxide Bridgman growth technique |
| ISSN号 | 0232-1300 |
| DOI | 10.1002/crat.200610803 |
| 通讯作者 | Xu, jiayue(crystalxu@mail.sic.ac.cn) |
| 英文摘要 | To grow zno single crystals from a high temperature solution of the zno-pbf2 system, a gas cooling system was assembled at the bottom of the crucible to induce nucleation in the initial growth stage. the growth experiments were carried out in a homemade vertical bridgman furnace and pt crucible of 28 mm in diameter was used. the furnace temperature was set to 1100 degrees c and the flow rate of the oxygen gas was optimized as 3.0 l/min. zno crystal up to 5 similar to 8mm in the thickness was obtained with the lowering rate of 0.3 mm/h. xrd patterns showed that the as-grown crystal was pure zno wurtzite phase. the impurity ions were analyzed by the glow discharge mass spectroscopy (gdms) as 390.0 ppm and 40.0 ppm for pb2+ and f-, respectively. (c) 2007 wiley-vch verlag gmbh & co. kgaa, weinheim. |
| WOS关键词 | VAPOR TRANSPORT |
| WOS研究方向 | Crystallography |
| WOS类目 | Crystallography |
| 语种 | 英语 |
| WOS记录号 | WOS:000244879600003 |
| 出版者 | WILEY-V C H VERLAG GMBH |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2382756 |
| 专题 | 中国科学院大学 |
| 通讯作者 | Xu, Jiayue |
| 作者单位 | 1.Chinese Acad Sci, Shanghai Inst Ceram, Shanghai 200050, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100039, Peoples R China |
| 推荐引用方式 GB/T 7714 | Li, Xinhua,Xu, Jiayue,Jin, Min,et al. Growth of zno single crystals by an induced nucleation from a high temperature solution of the zno-pbf2 system[J]. Crystal research and technology,2007,42(3):221-226. |
| APA | Li, Xinhua,Xu, Jiayue,Jin, Min,Wu, Xianjun,Qian, Guoxing,&Li, Xiaomin.(2007).Growth of zno single crystals by an induced nucleation from a high temperature solution of the zno-pbf2 system.Crystal research and technology,42(3),221-226. |
| MLA | Li, Xinhua,et al."Growth of zno single crystals by an induced nucleation from a high temperature solution of the zno-pbf2 system".Crystal research and technology 42.3(2007):221-226. |
入库方式： iSwitch采集
来源：中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。