Controlled synthesis and optical properties of colloidal ternary chalcogenide cuins2 nanocrystals
文献类型：期刊论文
| 作者 | Zhong, Haizheng1,2; Zhou, Yi1,2; Ye, Mingfu1,2; He, Youjun1,2; Ye, Jianping3; He, Chang1; Yang, Chunhe1; Li, Yongfang1 |
| 刊名 | Chemistry of materials
 |
| 出版日期 | 2008-10-28 |
| 卷号 | 20期号:20页码:6434-6443 |
| ISSN号 | 0897-4756 |
| DOI | 10.1021/cm8006827 |
| 通讯作者 | Li, yongfang(liyf@iccas.ac.cn) |
| 英文摘要 | A facile method for the synthesis of size- and shape-controlled cutns(2) semiconductor nanocrystals was developed by thermolysis of a mixed solution of cuac. in(ac)(3) (molar ratio of cuac to in(ac)(3) = 1: 1) and dodecanethiol in noncoordinating solvent 1-octadecene (ode) at 240 degrees c. cuins2 nanoparticles with size of 2 to similar to 5 nm and nanorods with aspect ratio of 1 to similar to 3 were obtained by adjusting the reaction parameters such as temperature and time. the as-prepared nanoparticles were characterized by x-ray diffraction (xrd), x-ray photoelectron spectroscopy (xps), transmission electron microscopy, selected area electron diffraction spectroscopy, inductively coupled plasma atomic emission spectroscopy, uv-vis absorption, and photoluminescence (pl) spectroscopy. the nanoparticle solutions exhibit tunable absorption and pl spectra with the absorption edge ranging from 550 to 750 nm and pl emission peaks from 600 to 750 rim, indicating a strong size-dependent quantum confinement effect. optical measurements of the cuins2) nanoparticles demonstrated that their optical properties are related to donor-acceptor defects, size-dependent quantum confined effects. and surface defects. the pl decay curve of cuins2 nanoparticles has a triple exponential characteristic with lifetimes of 4-12. 28-60, and 140-300 ns, respectively, and the pl emission with the longest lifetime (140-300 ns) occupied 40-80% of the pl emission of the samples. these results imply that the room-temperature pl emission of cuins2 nanoparticles involves three types of recombination: band exciton recombination, surface-related recombination, and donor-acceptor defects recombination. among them, the pl emission from donor-acceptor defects occupied a large amount. |
| WOS关键词 | SINGLE-SOURCE PRECURSORS ; COPPER-INDIUM SULFIDE ; ONE-POT SYNTHESIS ; FILM SOLAR-CELLS ; SEMICONDUCTOR NANOCRYSTALS ; QUANTUM DOTS ; THIN-FILM ; PHOTOPHYSICAL PROPERTIES ; FACILE ROUTE ; NANOPARTICLES |
| WOS研究方向 | Chemistry ; Materials Science |
| WOS类目 | Chemistry, Physical ; Materials Science, Multidisciplinary |
| 语种 | 英语 |
| 出版者 | AMER CHEMICAL SOC |
| WOS记录号 | WOS:000260254400027 |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2393172 |
| 专题 | 中国科学院大学 |
| 通讯作者 | Li, Yongfang |
| 作者单位 | 1.Chinese Acad Sci, Beijing Natl Lab Mol Sci, Key Lab Organ Solids, Inst Chem, Beijing 100190, Peoples R China 2.Chinese Acad Sci, Grad Univ, Beijing 10003, Peoples R China 3.Chinese Acad Sci, Key Lab Photochem, Inst Chem, Beijing 100080, Peoples R China |
| 推荐引用方式 GB/T 7714 | Zhong, Haizheng,Zhou, Yi,Ye, Mingfu,et al. Controlled synthesis and optical properties of colloidal ternary chalcogenide cuins2 nanocrystals[J]. Chemistry of materials,2008,20(20):6434-6443. |
| APA | Zhong, Haizheng.,Zhou, Yi.,Ye, Mingfu.,He, Youjun.,Ye, Jianping.,...&Li, Yongfang.(2008).Controlled synthesis and optical properties of colloidal ternary chalcogenide cuins2 nanocrystals.Chemistry of materials,20(20),6434-6443. |
| MLA | Zhong, Haizheng,et al."Controlled synthesis and optical properties of colloidal ternary chalcogenide cuins2 nanocrystals".Chemistry of materials 20.20(2008):6434-6443. |
入库方式： iSwitch采集
来源：中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。