Reactive formation of zircon inclusion pigments by deposition and subsequent annealing of a zirconia and silica double shell
文献类型:期刊论文
作者 | Zhao, Feng1,2; Gao, Yanfeng1; Luo, Hongjie1 |
刊名 | Langmuir |
出版日期 | 2009-12-01 |
卷号 | 25期号:23页码:13295-13297 |
ISSN号 | 0743-7463 |
DOI | 10.1021/la903197t |
通讯作者 | Gao, yanfeng(yfgao@mail.sic.ac.cn) |
英文摘要 | A novel general method for coating particles with a complex oxide was described. zirconia precursor and silica layers with careful control of film thickness were coated separately onto hematite particles in corresponding solutions. a zircon shell was subsequently obtained by heat treatment at 800 degrees c for 3 h using lif as a mineralizer. the as-prepared zirconoccluded hematite pigment gave a pink color to the glazed sample after annealing at 1120 degrees c. the current research suggests that various chromophoric particles can be encapsulated with zircon to prepare ceramic pigments for high-temperature use. |
WOS关键词 | SOL-GEL PROCESS ; CORE-SHELL ; AMORPHOUS SILICA ; DRUG-DELIVERY ; NANOPARTICLES ; PARTICLES ; MECHANISM ; SPHERES ; ROUTE |
WOS研究方向 | Chemistry ; Materials Science |
WOS类目 | Chemistry, Multidisciplinary ; Chemistry, Physical ; Materials Science, Multidisciplinary |
语种 | 英语 |
出版者 | AMER CHEMICAL SOC |
WOS记录号 | WOS:000271947700005 |
URI标识 | http://www.irgrid.ac.cn/handle/1471x/2397317 |
专题 | 中国科学院大学 |
通讯作者 | Gao, Yanfeng |
作者单位 | 1.Chinese Acad Sci, Shanghai Inst Ceram, Shanghai 200050, Peoples R China 2.Chinese Acad Sci, Grad Sch, Beijing 100049, Peoples R China |
推荐引用方式 GB/T 7714 | Zhao, Feng,Gao, Yanfeng,Luo, Hongjie. Reactive formation of zircon inclusion pigments by deposition and subsequent annealing of a zirconia and silica double shell[J]. Langmuir,2009,25(23):13295-13297. |
APA | Zhao, Feng,Gao, Yanfeng,&Luo, Hongjie.(2009).Reactive formation of zircon inclusion pigments by deposition and subsequent annealing of a zirconia and silica double shell.Langmuir,25(23),13295-13297. |
MLA | Zhao, Feng,et al."Reactive formation of zircon inclusion pigments by deposition and subsequent annealing of a zirconia and silica double shell".Langmuir 25.23(2009):13295-13297. |
入库方式: iSwitch采集
来源:中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。