Effect of anodic oxidation on the properties of ni-coated carbon fibers produced by electrodeposition
文献类型：期刊论文
| 作者 | Lu Xiao-xuan1,2,3; Lu Chun-xiang1,2; Yang Yu1,2; Zhou Pu-cha1,2,3; An Feng1,2,3; He Fu1,2 |
| 刊名 | New carbon materials
 |
| 出版日期 | 2010-12-01 |
| 卷号 | 25期号:6页码:454-459 |
| 关键词 | Carbon fiber Aanodic oxidation Ni coating Grain size Oxidation behavior |
| ISSN号 | 1007-8827 |
| 通讯作者 | Lu chun-xiang(lucx@sxicc.ac.cn) |
| 英文摘要 | Pan-based carbon fibers were continuously treated by anodic oxidation followed by electrodeposition of ni on their surface. the influence of anodic oxidation on mechanical properties, surface morphology, amount of surface acidic groups and growth mode of the ni coating were studied by sem, xrd, tg and conductometric titration. results showed that the total amount of surface acidic groups on the oxidized carbon fibers is about 10 times as large as that of the untreated ones and the tensile strength of carbon fibers decreased slowly at first and then quickly with increasing depth of oxidation. the growth mode of the ni coating changed from a volmer-weber mode to a frank-van der merwe mode and the grain size of the ni coating decreased from 14.5 to 11.2 nm for the untreated and treated carbon fibers respectively. the oxidation resistance of the carbon fibers was improved by the ni coating. the initial oxidation temperature of the ni-coated treated-carbon fibers with anodic oxidation is about 50 degrees c higher than that of the ni-coated carbon fibers without the oxidation. appropriate oxidation could improve the adhesion between the ni coating and the carbon fibers. |
| WOS关键词 | SURFACE ; COMPOSITES |
| WOS研究方向 | Materials Science |
| WOS类目 | Materials Science, Multidisciplinary |
| 语种 | 英语 |
| WOS记录号 | WOS:000286154900009 |
| 出版者 | SCIENCE CHINA PRESS |
| URI标识 | http://www.irgrid.ac.cn/handle/1471x/2408603 |
| 专题 | 中国科学院大学 |
| 通讯作者 | Lu Chun-xiang |
| 作者单位 | 1.Natl Engn Lab Carbon Fiber Technol, Taiyuan 030001, Peoples R China 2.Chinese Acad Sci, Inst Coal Chem, Key Lab Carbon Mat, Taiyuan 030001, Peoples R China 3.Chinese Acad Sci, Grad Univ, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Lu Xiao-xuan,Lu Chun-xiang,Yang Yu,et al. Effect of anodic oxidation on the properties of ni-coated carbon fibers produced by electrodeposition[J]. New carbon materials,2010,25(6):454-459. |
| APA | Lu Xiao-xuan,Lu Chun-xiang,Yang Yu,Zhou Pu-cha,An Feng,&He Fu.(2010).Effect of anodic oxidation on the properties of ni-coated carbon fibers produced by electrodeposition.New carbon materials,25(6),454-459. |
| MLA | Lu Xiao-xuan,et al."Effect of anodic oxidation on the properties of ni-coated carbon fibers produced by electrodeposition".New carbon materials 25.6(2010):454-459. |
入库方式： iSwitch采集
来源：中国科学院大学
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。