Fabrication and characterization of anode catalyst layers with structural variations for DMFC
文献类型：期刊论文
| 作者 | Ren,Tongqun3,4; Wang,Dazhi3,4; Shi,Peng3; Sun,Gongquan1; Zhou,Peng3; Mao,Qing5; Liang,Junsheng3,4; Wang,Suli1; Li,Yang2 |
| 刊名 | Materials Research Express
 |
| 出版日期 | 2018-04-27 |
| 卷号 | 5期号:4 |
| 关键词 | direct methanol fuel cell catalyst layer electrohydrodynamic jet layer-by-layer deposition |
| ISSN号 | 2053-1591 |
| DOI | 10.1088/2053-1591/aabdc5 |
| 英文摘要 | Abstract In this work, the electrohydrodynamic jet (E-Jet) Layer-by-Layer (LbL) deposition technique was employed to produce anode catalyst layer (CL) structure for direct methanol fuel cells (DMFC). The CLs with different thickness and porosity were fabricated with the control of the E-Jet deposition parameters. Then, the deposited anode CLs with structural variations were assembled to membrane electrode assemblies (MEAs). The results showed that the anode CL with higher porosity contributed higher dispersed catalyst, which further induced greater electrochemical active surface area (ESA) and higher performance. At optimized working condition the anode CL with high-dispersed catalyst of was produced using the E-Jet LbL deposition technique. It was observed that the peak power density is 72.8 mW cm?2 for the cell having a porosity of 0.63, which has an increase of about 33% after modification of the CL structure. |
| 语种 | 英语 |
| WOS记录号 | IOP:2053-1591-5-4-AABDC5 |
| 出版者 | IOP Publishing |
| 源URL | [http://cas-ir.dicp.ac.cn/handle/321008/167066]  |
| 专题 | 大连化学物理研究所_中国科学院大连化学物理研究所 |
| 作者单位 | 1.Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian, 116023, People’s Republic of China 2.NR Electric Power Electronics Co., Ltd, Changzhou, 213025, People’s Republic of China 3.Key Laboratory for Micro/Nano Technology and System of Liaoning Province, Dalian University of Technology, Dalian, 116024, People’s Republic of China 4.Key Laboratory for Precision and Non-traditional Machining Technology of Ministry of Education, Dalian University of Technology, Dalian, 116024, People’s Republic of China 5.Department of Electrochemical Engineering, Dalian University of Technology, Dalian, 116024, People’s Republic of China |
| 推荐引用方式 GB/T 7714 | Ren,Tongqun,Wang,Dazhi,Shi,Peng,et al. Fabrication and characterization of anode catalyst layers with structural variations for DMFC[J]. Materials Research Express,2018,5(4). |
| APA | Ren,Tongqun.,Wang,Dazhi.,Shi,Peng.,Sun,Gongquan.,Zhou,Peng.,...&Li,Yang.(2018).Fabrication and characterization of anode catalyst layers with structural variations for DMFC.Materials Research Express,5(4). |
| MLA | Ren,Tongqun,et al."Fabrication and characterization of anode catalyst layers with structural variations for DMFC".Materials Research Express 5.4(2018). |
入库方式： OAI收割
来源：大连化学物理研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。