Effect of yttrium addition on microstructures, damping properties and mechanical properties of as-cast Mg-based ternary alloys
文献类型：期刊论文
| 作者 | Niu, Rui-long1,2; Yan, Fang-jia1,2; Duan, Dong-ping1,2; Yang, Xue-min1,2 |
| 刊名 | JOURNAL OF ALLOYS AND COMPOUNDS
 |
| 出版日期 | 2019-05-15 |
| 卷号 | 785页码:1270-1278 |
| ISSN号 | 0925-8388 |
| 关键词 | Effect of yttrium Damping properties Mechanical properties Damping mechanism As-cast Mg-Zr-Y ternary alloys Microstructures |
| DOI | 10.1016/j.jallcom.2019.01.287 |
| 英文摘要 | In order to reveal the functions of yttrium addition on damping and mechanical properties for Mg-based alloys, the damping and mechanical properties of prepared as-cast Mg-0.6Zr-xY ternary alloys with [Y] = 1.0, 2.0, 3.0, 4.0 and 5.0 mass % have been experimentally measured and theoretically explained through combining the observed microstructures with related theoretical models or mechanisms. The experimental results indicate that added [Y] in the ternary alloys has clear effect on grain refinement. Changing [Y] from 1.0 to 5.0 mass % can effectively decrease the average size of formed equiaxed alpha-Mg grains from 70.15 to 33.62 mu m. The bulk-shaped yttrium-rich phase in alpha-Mg matrix is mainly composed of Mg24Y5 phase. Increasing [Y] from 1.0 to 5.0 mass % can significantly affect damping properties described by tan phi under the condition of epsilon> epsilon(cr) = 2.0 x 10(-2) , while no visible effect of increasing [Y] on tan phi at epsilon < epsilon(cr) = 2.0 x 10(-2) can be obtained. Furthermore, the influence of changing strain epsilon from 1.0 x 10(-4) to 1.0 x 10(-1) on tan phi complies with dislocation pinning theory or the G-L model. Meanwhile, increasing [Y] in the ternary alloys shows the similar variation tendency for relationship between tan phi and temperature T from ambient temperature T-am to 673 K (400 degrees C). The effect of varying temperature T from T-am to 673 K (400 degrees C) on tan phi for the ternary alloys can be well explained by the grain boundary damping mechanism. In addition, increasing [Y] from 1.0 to 4.0 mass % can effectively promote both yield strength R-p0.2 and ultimate tensile strength R-m, however further increasing [Y] from 4.0 to 5.0 mass % cannot result in an obviously increasing tendency for R-p0.(2) and R-m. The similar results of adding [Y] on elongation A can also be obtained with [Y] = 3.0% as a criterion. Meanwhile, the measured results of adding [Y] on Rp(0.2) and R-m for the ternary alloys can be well explained by the grain boundary strengthening and solid solution strengthening mechanisms. Therefore, the optimal chemical composition for as-cast Mg-Zr-Y ternary alloys with higher damping properties and greater tensile properties is recommended to be Mg-0.6Zr-4.0Y. (C) 2019 Elsevier B.V. All rights reserved. |
| WOS关键词 | BEHAVIOR ; DEFORMATION ; DISLOCATION ; PHASES ; ND ; RE |
| 资助项目 | Beijing Natural Science Foundation[2182069] ; National Natural Science Foundation of China[51174186] |
| WOS研究方向 | Chemistry ; Materials Science ; Metallurgy & Metallurgical Engineering |
| 语种 | 英语 |
| 出版者 | ELSEVIER SCIENCE SA |
| WOS记录号 | WOS:000460386900151 |
| 资助机构 | Beijing Natural Science Foundation ; National Natural Science Foundation of China |
| 源URL | [http://ir.ipe.ac.cn/handle/122111/28201]  |
| 专题 | 中国科学院过程工程研究所 |
| 通讯作者 | Duan, Dong-ping; Yang, Xue-min |
| 作者单位 | 1.Chinese Acad Sci, Inst Proc Engn, CAS Key Lab Green Proc & Engn, Beijing 100190, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Niu, Rui-long,Yan, Fang-jia,Duan, Dong-ping,et al. Effect of yttrium addition on microstructures, damping properties and mechanical properties of as-cast Mg-based ternary alloys[J]. JOURNAL OF ALLOYS AND COMPOUNDS,2019,785:1270-1278. |
| APA | Niu, Rui-long,Yan, Fang-jia,Duan, Dong-ping,&Yang, Xue-min.(2019).Effect of yttrium addition on microstructures, damping properties and mechanical properties of as-cast Mg-based ternary alloys.JOURNAL OF ALLOYS AND COMPOUNDS,785,1270-1278. |
| MLA | Niu, Rui-long,et al."Effect of yttrium addition on microstructures, damping properties and mechanical properties of as-cast Mg-based ternary alloys".JOURNAL OF ALLOYS AND COMPOUNDS 785(2019):1270-1278. |
入库方式： OAI收割
来源：过程工程研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。