Investigation of the mechanical and thermal properties of LFR PA66 with graphene coating on fibre surface
文献类型：期刊论文
| 作者 | Jin, S.-Y.1; Du, W.-W.2; Benkhenafou, F.3; Douadji, Lyes4 |
| 刊名 | International Polymer Processing
 |
| 出版日期 | 2018 |
| 卷号 | 33期号:2页码:286-291 |
| ISSN号 | 0930777X |
| DOI | 10.3139/217.3604 |
| 英文摘要 | An industrial fibreglass winding process is employed to apply graphene based sizing (0.2 wt% graphene concentration) on fibreglass surface. Both SEM and Raman spectroscopy characterization have proved that the coating of graphene on fibreglass surface is homogeneous and that the roughness of the fibreglass surface was improved. Long fiberglass-graphene reinforced PA66 pellets are successfully prepared through a pultrusion process. LGF-graphene-PA66 composites are produced following an injection molding process. Thermal conductivity was found to increase from 0.23 W/ m · K–1to 0.67 W/m · K–1when compared with samples without graphene coating. The tensile strength of LGF-graphene-PA66 is 196 MPa while that of LGF-PA66 is 173 MPa. Tensile modulus is also found to increase to 13.5 GPa from 10.6 GPa after graphene coating. This new graphene coating process is a good method to produce high performance composites. © Carl Hanser Verlag, Munich. |
| 语种 | 英语 |
| 源URL | [http://119.78.100.138/handle/2HOD01W0/7985]  |
| 专题 | 中国科学院重庆绿色智能技术研究院 |
| 作者单位 | 1.Luojiang Jinhua Fibreglass, Deyang City; Sichuan Province, China; 2.College of Material Science and Engineering, Southwest University, Chongqing, China; 3.Department of Physical, University of Tlemcen, Tlemcen, Algeria; 4.Chongqing Institute of Green and Intelligent Technology, Chinese Academy of Sciences, Chongqing, China |
| 推荐引用方式 GB/T 7714 | Jin, S.-Y.,Du, W.-W.,Benkhenafou, F.,et al. Investigation of the mechanical and thermal properties of LFR PA66 with graphene coating on fibre surface[J]. International Polymer Processing,2018,33(2):286-291. |
| APA | Jin, S.-Y.,Du, W.-W.,Benkhenafou, F.,&Douadji, Lyes.(2018).Investigation of the mechanical and thermal properties of LFR PA66 with graphene coating on fibre surface.International Polymer Processing,33(2),286-291. |
| MLA | Jin, S.-Y.,et al."Investigation of the mechanical and thermal properties of LFR PA66 with graphene coating on fibre surface".International Polymer Processing 33.2(2018):286-291. |