Synthesis and structure-property relationships of polypropylene-g-polystyrene and polypropylene-g-poly(n-butyl acrylate) graft copolymers with well-defined molecular structures
文献类型：期刊论文
| 作者 | Wang, Lu1,2; Yang, Hongfan1,2; Tan, Haiying1,2; Yao, Kun1,2; Gong, Jiang1,2; Wan, Dong1,2; Qiu, Jian1; Tang, Tao1 |
| 刊名 | POLYMER
 |
| 出版日期 | 2013-06-01 |
| 卷号 | 54期号:14页码:3641-3653 |
| 关键词 | Pp-based Graft Copolymer Rheology Foam |
| ISSN号 | 0032-3861 |
| DOI | 10.1016/j.polymer.2013.05.024 |
| 英文摘要 | Several polypropylene-g-polystyrene (PP-g-PS) and polypropylene-g-poly(n-butyl acrylate) (PP-g-PnBA) graft copolymers with well-defined molecular structures, basing on the same PP-Br precursor, were synthesized via a combination of metallocene-catalyzed polymerization and ATRP. The structure -property relationships of the resultant graft copolymers were systematically investigated. The crystallization temperatures of the obtained PP-g-PS and PP-g-PnBA graft copolymers decreased first and increased then with the enhancement of branch lengths. Compared to PP-Br, the introduction of PS or PnBA branches onto PP backbones both led to increased eta(0), more pronounced shear-thinning behavior, elevated value of G' at low shear frequencies, and reduced loss angle. Under the same foaming conditions, the resulting PP-g-PS and PP-g-PnBA foams exhibited closed cell structure, increased cell density, and uniformized cell size distribution compared to the PP-Br foam. The cell density of PP-g-PS foam increased first and decreased then with the enhancement of branch length, and the cell size increased as the branch length increased. However, the cell density of the obtained three PP-g-PnBA foams was almost the same regardless of the PnBA branch length, and the cell size decreased first and increased then with increasing the branch length. (C) 2013 Elsevier Ltd. All rights reserved. |
| 语种 | 英语 |
| WOS记录号 | WOS:000320679600027 |
| 出版者 | ELSEVIER SCI LTD |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/46323]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Tang, Tao |
| 作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China 2.Univ Chinese Acad Sci, Beijing 100049, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang, Lu,Yang, Hongfan,Tan, Haiying,et al. Synthesis and structure-property relationships of polypropylene-g-polystyrene and polypropylene-g-poly(n-butyl acrylate) graft copolymers with well-defined molecular structures[J]. POLYMER,2013,54(14):3641-3653. |
| APA | Wang, Lu.,Yang, Hongfan.,Tan, Haiying.,Yao, Kun.,Gong, Jiang.,...&Tang, Tao.(2013).Synthesis and structure-property relationships of polypropylene-g-polystyrene and polypropylene-g-poly(n-butyl acrylate) graft copolymers with well-defined molecular structures.POLYMER,54(14),3641-3653. |
| MLA | Wang, Lu,et al."Synthesis and structure-property relationships of polypropylene-g-polystyrene and polypropylene-g-poly(n-butyl acrylate) graft copolymers with well-defined molecular structures".POLYMER 54.14(2013):3641-3653. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。