Miscibility, Crystallization, and Morphology of the Double-Crystalline Blends of Insulating Polyethylene and Semiconducting Poly(3-Butylthiophene)
文献类型：期刊论文
| 作者 | Wang, Yuzhen1,2,3; Chen, Zhaobin1; Chen, Jiayue1,2,3; Qu, Yunpeng1,2,3; Yang, Xiaoniu1,2 |
| 刊名 | JOURNAL OF MACROMOLECULAR SCIENCE PART B-PHYSICS
 |
| 出版日期 | 2013-09-01 |
| 卷号 | 52期号:10页码:1388-1404 |
| 关键词 | Blend Poly(3-butylthiophene) Polyethylene Preferred Orientation Ringed Spherulite |
| ISSN号 | 0022-2348 |
| DOI | 10.1080/00222348.2013.768506 |
| 英文摘要 | A series of crystalline semiconducting poly(3-butylthiophene) (P3BT)/crystalline insulating polyethylene (PE) blends were prepared and the miscibility, crystallization, and structure/morphology were investigated. Even though phase separation was observed by transmission electron microscopy (TEM) and small-angle X-ray scattering (SAXS), several pieces of evidence indicated that limited miscibility should be present in PE/P3BT blends: small changes in both T-m and crystallinity of PE phase and a small portion of PE being dissolved in P3BT. The study of PE isothermal crystallization kinetics revealed that the introduction of P3BT significantly influenced the nucleation mechanism and growth geometry, i.e., PE was transformed from three-dimensional (3D) spherulitic to two-dimensional (2D) disc crystals. A striking reduction of nucleation density and an obvious ringed morphology of PE spherulites (2D) in PE/P3BT blends were also observed by polarized optical microscopy; it is proposed that the limited miscibility between PE and crystalline P3BT favors the formation of ringed PE spherulite in the blends. Additionally, preferred orientation of PE lamellae, with their b-axis largely constrained to the thin film plane, was observed by X-ray diffraction in PE/P3BT blend films. It is evidenced that the PE orientation was due to the b-axis being the crystal growth direction, which can only be in film plane. |
| 语种 | 英语 |
| WOS记录号 | WOS:000319722700003 |
| 出版者 | TAYLOR & FRANCIS INC |
| 源URL | [http://ir.iccas.ac.cn/handle/121111/46617]  |
| 专题 | 中国科学院化学研究所 |
| 通讯作者 | Yang, Xiaoniu |
| 作者单位 | 1.Chinese Acad Sci, Changchun Inst Appl Chem, Polymer Composites Engn Lab, Changchun 130022, Peoples R China 2.Chinese Acad Sci, Changchun Inst Appl Chem, State Key Lab Polymer Phys & Chem, Changchun 130022, Peoples R China 3.Chinese Acad Sci, Grad Sch, Beijing, Peoples R China |
| 推荐引用方式 GB/T 7714 | Wang, Yuzhen,Chen, Zhaobin,Chen, Jiayue,et al. Miscibility, Crystallization, and Morphology of the Double-Crystalline Blends of Insulating Polyethylene and Semiconducting Poly(3-Butylthiophene)[J]. JOURNAL OF MACROMOLECULAR SCIENCE PART B-PHYSICS,2013,52(10):1388-1404. |
| APA | Wang, Yuzhen,Chen, Zhaobin,Chen, Jiayue,Qu, Yunpeng,&Yang, Xiaoniu.(2013).Miscibility, Crystallization, and Morphology of the Double-Crystalline Blends of Insulating Polyethylene and Semiconducting Poly(3-Butylthiophene).JOURNAL OF MACROMOLECULAR SCIENCE PART B-PHYSICS,52(10),1388-1404. |
| MLA | Wang, Yuzhen,et al."Miscibility, Crystallization, and Morphology of the Double-Crystalline Blends of Insulating Polyethylene and Semiconducting Poly(3-Butylthiophene)".JOURNAL OF MACROMOLECULAR SCIENCE PART B-PHYSICS 52.10(2013):1388-1404. |
入库方式： OAI收割
来源：化学研究所
浏览0
下载0
收藏0
其他版本
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。